Correlation between EPDM aging properties and climate as well as prediction of the distribution of EPDM aging degree in China [PDF]
, 2016 Based on the analysis of aging behavior of ethylene propylene diene rubber(EPDM) and the mechanism of action of climate on EPDM,the aging data of EPDM exposed for 3 years in 11 typical material weathering test stations and the meteorological data there ...
GAO Jin +4 more
core +1 more source
, 2019 利用紫外老化箱对三元乙丙橡胶（EPDM）进行紫外光老化试验,采用核磁共振氢谱（1H-NMR）与傅里叶红外光谱（FT-IR）两种表征方法,追踪EPDM紫外光老化过程的化学结构变化,探讨了EPDM的老化机理。结果表明:EPDM的紫外光老化始于第3单体中活泼氢的断裂,氧化生成含氧产物,进而影响整个分子链。EPDM的抗紫外光老化性能较差,随着老化时间的延长,第3单体中的活泼氢的含量迅速减小,羰基含量呈现非线性增加。EPDM在紫外光老化过程中发生Norrish Ⅱ型光化学反应,生成了端烯烃结构。老化过程中生成了醇、
丁玲 +6 more
core +1 more source
Research on Thermosensitive Coatings for Thermal Runaway Warning in Energy Storage Power Station [PDF]
, 2023 [Introduction] Lithium iron phosphate battery storage power plants are an important basis for new power systems to consume large-scale new energy, however, the thermal runaway of battery cells seriously threatens the operational safety of storage power ...
Chaolu NIU +8 more
core +1 more source
, 2018 采用人工紫外光老化和自然老化2种方法对天然橡胶(NR)进行老化研究,利用傅里叶变换红外光谱、核磁共振波谱及紫外-可见光吸收光谱测试法对老化产物进行表征,探究了NR的老化机理。结果表明,天然橡胶抗紫外光老化能力较差,在紫外光下照射3 h,其分子结构即发生明显改变,而在自然老化的条件下,天然橡胶经过30 d结构才发生变化。天然橡胶的老化机理:双键α-H最先被活化,随后发生氧化生成醛酮等氧化产物,同时双键被加成,烯氢含量减少;老化过程中,氧化降解与交联反应同时存在,老化前期以降解为主,后期产生交联 ...
丁玲 +6 more
core +1 more source
, 2018 为了扩展传统铜锌铝催化剂在车载甲醇自热式重整（ATRM）制氢过程中的应用,采用反向共沉淀法制备了不同铜锌摩尔比的铜锌铝氧化物催化剂,并与工业铜锌铝催化剂SCST-401进行比较。结果发现,该类催化剂的性能随着铜锌摩尔比的增加而提高。其中,Cu30Zn10Al催化剂在200600℃范围内具有最佳的ATRM反应性能,而不含铜的催化剂Zn40Al在500600℃高温下具有与Cu20Zn20Al和Cu10Zn30Al相近的活性。此外,Cu30Zn10Al催化剂与商用催化剂SCST-401的甲醇转化率也相近 ...
刘运权 +5 more
core +1 more source
, 2019 对聚乙烯醇缩丁醛（PVB）进行热氧老化试验,采用三种表征方法,从化学结构变化的角度对PVB的热氧老化机理进行研究。研究结果表明:PVB的抗热氧老化性能较差,其羟基、羰基、缩丁醛基均对热敏感。老化前期PVB主要发生降解,首先是在热的作用下,羟基氧化、酯基分解、缩醛环受热开环生成烷氧自由基,然后生成酮、醛,生成的自由基可以诱导分子链断裂并夺取PVB中活泼的氢原子进而又生成自由基。老化后期PVB老化反应以交联为主。热氧老化1d即生成醛,羟基、酯羰基开始减少,老化2 d生成酮,缩醛环老化6 d急剧减少 ...
丁玲 +4 more
core +1 more source
Evolution of free radicals in ultra-high molecular weight polyethylene irradiated by an electron beam during accelerated aging process [PDF]
Irradiated medical ultra-high molecular-weight polyethylene (UHMWPE) must be validated through accelerated aging tests to meet the requirements for implantation into the human body.
HU Zhijie +5 more
core +1 more source
, 2019 文中对顺丁橡胶进行热氧老化研究,采用核磁共振氢谱、傅里叶变换衰减全反射红外光谱、紫外-可见光吸收光谱法3种谱学法对老化产物进行表征。追踪顺丁橡胶在老化过程中化学结构的变化,进而探究其老化机理。结果表明,顺丁橡胶的抗热氧老化能力较差,在120℃老化0.5 d时,其结构即发生明显变化,烯烃含量明显下降,生成醇及醛酮化合物,老化15 d时顺丁橡胶双键α-H已反应约97%。热氧老化反应机理为双键α-H先发生氧化形成过氧化羟基,进而氧化成醇及醛酮化合物,最终降解生成末端丙烯醛,同时双键发生自由基加成反应 ...
丁玲 +4 more
core +1 more source
Correlation between Outdoor-exposure and Indoor-accelerated Ageing Test for Epoxy Coating [PDF]
, 2006 通过室外海洋大气暴晒和室内紫外线照射对环氧涂层进行了老化试验,并运用光泽、颜色、粉化率、SEM以及电化学多重动电位扫描(MCPDP)等手段测试了涂层在室外大气暴晒和室内紫外加速老化下的表面形貌和对金属保护性能的变化,初步探讨室外海洋大气暴晒和室内紫外人工老化试验的相关性。发现对于环氧涂层室内紫外人工老化降解的效果强于室外海洋大气天然老化,基于光泽测试的加速因子约为5;基于颜色和粉化率测试的加速因子都大于12。The outdoor-exposure test and indoor-accelerated
叶美琪 +4 more
core
Research and Design of Multi-Channel Temperature Control System for High Power LEDs Online Accelerated Aging [PDF]
, 2016 半导体照明技术伴随时代的进步，应用愈发广泛，大功率LED照明领域更是逐步走向普及。但实际应用中，LED器件和封装的缺陷及工作时发热极大限制了其性能和实际寿命，可靠性问题日渐显露。为此LED寿命加速测试尤为重要，以实现寿命预测，失效机理分析，使得LED可靠性提升。常用的高温老化测试传统上使用高温试验箱，此方法存在诸多缺点：参数检测不连续、温升慢、体积大、功耗高。本文针对性地研制了一套轻便的LED在线寿命加速多路温控系统（以下简称温控系统）。主要工作内容与研究成果如下： 1.研制了温控系统的硬件部分 ...
周骁炀
core