Advanced Engineering Materials, EarlyView.The presented study focuses on the fracture behaviour of carbon‐bonded magnesia MgO–C refractories, where environmentally friendly fructose, collagen and lignin serve as temporary binding agents. The partial substitution of the source material with recycled MgO–C reduces the fracture resistance, which can be counteracted by the additional introduction ...
Marc Neumann +6 more
wiley +1 more source
Advanced Engineering Materials, EarlyView.Four‐point bending tests are conducted in an argon atmosphere on commercial MgO‐C brick grades with and without MgO‐C recyclate from room temperature up to 1300 °C. No detrimental effect of the MgO‐C recyclates on bending strength is found. Instead, a decisive influence of the total carbon content is observed, with lower total carbon contents ...
Alexander Schramm +5 more
wiley +1 more source
Advanced Engineering Materials, EarlyView.This study investigates thermo‐chemical processes during high‐temperature testing of two commercial MgO‐C brick grades, one containing 47.5 wt.% MgO‐C recyclate. Using ETV, DTA/TG‐MS, XRD, and SEM/EDS/EBSD, mechanisms such as carbothermal reduction of magnesia, impurity incorporation into the secondary MgO surface layer, and calcium‐rich phase ...
Alexander Schramm +6 more
wiley +1 more source
Thermophysical Properties of the Desulphurization Slags With Various CaS and CaO/Al2O3 Ratio
Advanced Engineering Materials, EarlyView.This article investigates how CaS content and the CaO/Al2O3 ratio influence the thermophysical properties of desulphurization slags. Using experimental measurements and thermodynamic simulations, this study reveals complex effects on viscosity, surface tension, and density, providing new insight into slag structure and phase behavior under ...
Eldar Salpagarov +4 more
wiley +1 more source
Advanced Engineering Materials, EarlyView.Carbon‐free inert anodes are essential for decarbonizing aluminum electrolysis. This study investigates a recyclate‐based MgO‐316L steel composite anode tested under galvanostatic Hall–Héroult conditions in cryolite at 1000°C. Microstructural analysis reveals selective MgO fluorination, spinel and oxide layer formation, electrolyte infiltration, and ...
Serhii Yaroshevskyi +7 more
wiley +1 more source
Advanced Engineering Materials, EarlyView.The formation of nonmetallic inclusions (NMIs) was investigated in this study, carrying out immersion tests for 30 min at a temperature of 1600°C with liquid high‐silicon electrical steel (Si ≈ 3 mass‐%) and different MgO–C refractories. Conventional MgO–C refractories were considered, as well as MgO–C refractories containing MgO–C recyclate and ...
Lukas Neubert +6 more
wiley +1 more source
Evaluating Energy Absorption Performance of Filled Lattice Structures
Advanced Engineering Materials, EarlyView.Maximum stress must be considered to robustly evaluate energy absorber designs. This approach was applied to compare all types of absorbers in a single Ashby diagram and determine the utility of filling lattice voids with a second material. High‐performance fillers can improve the performance of lattices that are limited by buckling or catastrophic ...
Christian Bonney +2 more
wiley +1 more source
Advanced Engineering Materials, EarlyView.Through direct application of porous transport layer (PTL) on the bipolar plate (BPP) with thermal spraying, the interfacial contact resistance is improved. With the cold gas sprayed BPP–PTL coating system, a proton exchange membrane water electrolysis cell with a cell voltage of Ucell = 1.9 V can be operated up to i = 2.5 A/cm2 in a dynamic mode ...
Kirsten Bobzin +5 more
wiley +1 more source
Advanced Engineering Materials, EarlyView.EDX elemental map of the pre‐oxidized MgO–steel cermet anode cross section after electrolysis. The development of inert anodes for aluminum electrolysis remains challenging due to the high corrosivity of cryolite‐based melts at 950°C–1000°C. This study investigates the corrosion and process behavior of a carbon‐free MgO–steel cermet anode derived from ...
Alexander Adamczyk +7 more
wiley +1 more source
Advanced Engineering Materials, EarlyView.Micro‐Raman spectroscopy is applied to characterize corrosion products in a recycled‐based MgO–316L steel composite anode after molten salt electrolysis. A depth‐dependent Fe–O/Fe–Al–O layer sequence of magnetite, hercynite, and an Al‐doped magnetite transition zone is identified.
Felix Drechsler +9 more
wiley +1 more source