The mechanism of liquid copper deoxidation during argon blowing [PDF]

Metalurgija, 2009
Using the method of argon (with specified oxygen content) blowing, the possibility of copper deoxidation has been considered on the basis of specific thermodynamic data.
G. Siwiec, J. Willner
doaj  

Microstructure Modification of Additively Manufactured Mo–9Si–8B by Annealing and Its Effects on High‐Temperature Mechanical Properties

Advanced Engineering Materials, EarlyView.
Postbuild annealing systematically modifies the phase fractions and morphology of EB‐PBF processed Mo–9Si–8B. Quantitative microstructure–property correlations reveal how controlled phase evolution enhances high‐temperature compressive strength and creep resistance.
Christopher Schmidt, Yong Chen, Georg Hasemann, Benjamin Wahlmann, Carolin Körner, Manja Krüger   +5 more
wiley   +1 more source

Investigating the Effect of Inclination Angle and the Influence of Scan Parameters on the Appearance and Thermal and Mechanical Properties of Filigree Tension Rods of LPBF‐Manufactured NiTi Shape‐Memory Alloys

Advanced Engineering Materials, EarlyView.
This article investigates the dependence of the properties on the manufacturing orientation in the form of the inclination angle to the build plate of LPBF‐fabricated NiTi rods with a diameter of 150–220 µm. Metallographic, chemical, thermal, and mechanical characterization show behavior under identical manufacturing conditions that ranges from ...
Sandra Herzig, Michael Werner, Christian Rotsch   +2 more
wiley   +1 more source

Influence of TiC and TiN Ceramic Reinforcements on the Microstructure, Thermal Expansion Behavior, and Tensile Properties of Invar 36 Manufactured by Laser Powder Bed Fusion

Advanced Engineering Materials, EarlyView.
This study examines Invar composites reinforced with titanium carbide (TiC) and titanium nitride (TiN) using laser powder bed fusion (LPBF). It presents the influence of reinforcements on microstructure, tensile properties, and thermal expansion. Results show that TiC effectively strengthens Invar while maintaining low thermal expansion, whereas TiN ...
Ayodeji Nathaniel Oyedeji, Natasha Sacks, Johannes Pötschke, Björn Matthey   +3 more
wiley   +1 more source

The Influence of Nitrogen in Ar+N2 Mixture on Parameters of High-Temperature Device with Electric Arc

Acta Polytechnica, 2013
The paper presents the results of numerous experiments carried out on a high temperature device consisting of an arc heater with intensively blasted electric arc and reaction chambers connected to its output. The influence of nitrogen mass concentration (
Ivana Jakubova, Josef Senk, Ilona Laznickova   +2 more
doaj  

Rapidly Solidified High‐Strength Invar 36 Prepared by Planar‐Flow Melt Spinning

Advanced Engineering Materials, EarlyView.
The Invar 36 alloy was rapidly solidified using the planar‐flow melt‐spinning technique. Ribbon samples with thicknesses ranging from 20 to 160 mm were produced. As the grain size of the ribbon decreased to sub‐micron levels, the hardness increased by more than 2 times.
Bekir Akgül, Mehmet Kul
wiley   +1 more source

Argon Alleviates Bone Cancer Pain by Mitigating Neuronal Ferroptosis via the TLR2-COX-2 Pathway

Frontiers in Bioscience-Landmark
Background: Bone cancer pain (BCP) related neuronal damage is associated with ferroptosis, a regulated cell death dependent on iron. The noble gas argon is known to have neuroprotective effects, reducing neuroinflammation and enhancing
Peipei Kang, Gujun Cong, Xiaowen Meng, Yang Zhang, Haiyan Sun, Lei Wang, Chao Zhang, Junyi Ma, Tong Liu, Fuhai Ji   +9 more
doaj   +1 more source

Investigating the Low‐Temperature Phase Stability of the Binary Ta–W System

Advanced Engineering Materials, EarlyView.
Atomistic simulations show that the binary Ta–W system forms ordered intermetallic phases, B2‐TaW and D03‐TaW3, as 0 K ground states. Configurational entropy, however, lowers the free energy of the disordered bcc solid solution, which becomes the stable phase above about 400 K.
Klemens Lechner, Anna Sophie Jelinek, Velislava Terziyska, Peter Wagatha, Wolfram Knabl, Christian Mitterer, Helmut Clemens, David Holec   +7 more
wiley   +1 more source

Cryogenic Deformation Behavior of TiAl and Insights Into Embrittlement After High‐Temperature Exposure Combined With Secondary Ion Mass Spectroscopy of Near Surface Chemistry

Advanced Engineering Materials, EarlyView.
Near‐surface deuterium enrichment profiles for different microstructural types of TiAl after exposure at 700 °C in a heavy water‐containing environment. The deuterium levels are significantly higher than expected from natural occurrence, indicating that the heavy water dissociated during the exposure treatment and entered the specimens.
Jonathan D. H. Paul, Alexander Welle, Dirk Matthiessen, Michael Oehring, Fritz Appel, Florian Pyczak   +5 more
wiley   +1 more source

Enhancement of the Through‐Thickness Electrical Conductivity of Carbon‐Fiber‐Reinforced Plastics Using Large Graphite Particles

Advanced Engineering Materials, EarlyView.
To enhance through‐thickness conductivity without sacrificing impregnation, large spherical graphite particles are intentionally employed in a low‐viscosity resin. Unlike finer conductive fillers, these particles remain outside the fiber bundles and accumulate in resin‐rich interlaminar regions during molding.
Keito Hosoe, Yu Zhou, Shintaro Kamiyama, Takao Okada, Tomohiro Yokozeki, Ryoma Tokonami, Tatsuhiro Takahashi   +6 more
wiley   +1 more source