An evaluation of weld metal nitrogen retention and properties in 316NL austenitic stainless steel [PDF]
, 2011 A series of tests were conducted using varying levels of nitrogen and helium in a conventional argon shielding gas when welding 316LN austenitic stainless steel. The outcome was that a 15 per cent nitrogen addition to the argon shielding gas had the most
Baker, Thomas +2 more
core +4 more sources
Mechanical and Metallurgical Properties of Dissimilar Joining of 304 ASS: A Review [PDF]
E3S Web of Conferences, 2023 The mechanical and metallurgical properties of dissimilar joining of 304 stainless steel (SS) and other alloys have been extensively studied in recent years.
Anirudh Dhiraj M. +4 more
doaj +1 more source
Discussion on Causes and Solutions of the Biting Mechanism of Stainless Steel Bolts [PDF]
MATEC Web of Conferences, 2022 Due to the influence of the peculiar material characteristics, austenitic stainless steel bolts are always easy to be locked during disassembly. This is not only seriously affected the service performance of austenitic stainless steel bolts, but also ...
Zheng Jianjun, Chen Hao, Zhang Yanfei
doaj +1 more source
Study on the Critical Cl- Concentration for the Transition of Dominant Failure Mechanism of 304 Stainless Steel in OH- + Cl- Mixed Medium [PDF]
Cailiao Baohu, 2022 For studying the critical condition for the transition of the dominant failure mechanism of 304 austenitic stainless steel in OH-+ Cl- medium, the stress corrosion sensitivity of 304 austenitic stainless steel in the mediums of 10% NaOH and 15 ...
HU Pan, YAN Wei - li, AI Zhi - bin, KONG Wei - hai, ZHANG Qiang, HU Jiu - shao
doaj +1 more source
Finite element modelling of cold formed stainless steel columns [PDF]
, 2004 This paper describes the results obtained from a finite element investigation into the load capacity of column members of lipped channel cross-section, cold formed from Type 304 stainless steel, subjected to concentric and eccentric compression loading ...
Rhodes, J., Macdonald, M.
core +5 more sources
A multiscale constitutive model for intergranular stress corrosion cracking in type 304 austenitic stainless steel [PDF]
, 2013 Intergranular stress corrosion cracking (IGSCC) is a fracture mechanism in sensitised austenitic stainless steels exposed to critical environments where the intergranular cracks extends along the network of connected susceptible grain boundaries.
Rahimi, S, Siddiq, A
core +4 more sources
MIG WELDING OF AUSTENITIC 316L STEEL USED IN MEANS OF TRANSPORT [PDF]
Scientific Journal of Silesian University of Technology. Series Transport, 2022 The austenitic 316L steel (1.4401) is an important stainless material used to build various means of transport. Austenitic steel has high resistance to atmospheric corrosion.
Bożena SZCZUCKA-LASOTA, Tomasz WĘGRZYN
doaj +1 more source
Irradiation-induced BCC-phase formation and magnetism in a 316 austenitic stainless steel
Nuclear Engineering and Technology, 2020 Specimens of austenitic stainless steel were irradiated with 6 MeV Xe ions to two doses of 7 and 15 dpa at room temperature and 300 °C respectively. Then partial irradiated specimens were subsequently thermally annealed at 550 °C. Irradiation-induced BCC-
Chaoliang Xu +5 more
doaj +1 more source
Heliyon, 2023 To provide a theoretical basis for the design of super austenitic stainless steel used in flue gas desulfurization environment, by changing the Cu content in 00Cr20Ni18Mo6CuN super austenitic stainless steel to explore the influence of Cu on its ...
Bingbing Li +7 more
doaj +1 more source
Hydrogen Embrittlement Susceptibility of Super Duplex Stainless Steels [PDF]
, 2010 This thesis describes the metallurgical and environmental factors that influence hydrogen embrittlement of super duplex stainless steels and presents a model to predict the rate at which embrittlement occurs.
Alsarraf, Jalal
core +7 more sources