Four‐Point Bending Tests at High Temperatures on Commercial MgO‐C Refractory Bricks with and Without Recyclate Considering Different Carbon Contents

Advanced Engineering Materials, EarlyView.
Four‐point bending tests are conducted in an argon atmosphere on commercial MgO‐C brick grades with and without MgO‐C recyclate from room temperature up to 1300 °C. No detrimental effect of the MgO‐C recyclates on bending strength is found. Instead, a decisive influence of the total carbon content is observed, with lower total carbon contents ...
Alexander Schramm, Lukas Knöchel, Thomas Schemmel, Christos G. Aneziris, Anja Weidner, Horst Biermann   +5 more
wiley   +1 more source

The Influence of Orthodontic Bracket Base Design and Bonding System on Shear Bond Strength. [PDF]

J Funct Biomater
Nardin MM, Ionescu AG, Done AE, Mirițoiu CM, Pădeanu PA, Rauten AM, Dăguci L, Preoteasa CT, Mercuț V.   +8 more
europepmc   +1 more source

Sol–Gel Derived Polymer Precursors for Stereolithography of ZrC

Advanced Engineering Materials, EarlyView.
ZrC is a critical material target for extreme temperature conditions. This report describes a protocol for preparing ZrC ceramics via stereolithography and examines the impact of the polymer matrix on carbothermal reduction and mechanical stability of 3D printed ZrC.
Charles J. Rafalko, Evelyn Wang, Michael A. Hickner   +2 more
wiley   +1 more source

Accuracy of two 3D printed guide plates in bonding orthodontic brackets. [PDF]

BMC Oral Health
Jin M, Zhang Y, Tang R, Song W, Chen Y, Lu S, Han M.   +6 more
europepmc   +1 more source

Investigation of Thermo‐Chemical Processes in Commercial MgO‐C Refractory Bricks With and Without MgO‐C Recyclate at Elevated Temperatures

Advanced Engineering Materials, EarlyView.
This study investigates thermo‐chemical processes during high‐temperature testing of two commercial MgO‐C brick grades, one containing 47.5 wt.% MgO‐C recyclate. Using ETV, DTA/TG‐MS, XRD, and SEM/EDS/EBSD, mechanisms such as carbothermal reduction of magnesia, impurity incorporation into the secondary MgO surface layer, and calcium‐rich phase ...
Alexander Schramm, Jana Hubálková, Christian Schimpf, Thomas Schemmel, Christos G. Aneziris, Anja Weidner, Horst Biermann   +6 more
wiley   +1 more source

Immediate vs. delayed bonding to bleached enamel: an in-vitro evaluation of nanoscopic changes and bond strength. [PDF]

BMC Oral Health
Saleem A, Hasan SR, Jabeen N, Musharraf S, Shafique HZ, Bibi K.   +5 more
europepmc   +1 more source

Removing Oxide Layers and Retaining Oxide‐Free Steel Surfaces by Polishing in Oxygen‐Free Atmosphere

Advanced Engineering Materials, EarlyView.
In this study, the efficacy of wet mechanical polishing under an oxygen‐free atmosphere for deoxidation and the retention of an oxide‐free steel surface are elucidated using X‐ray photoelectron spectroscopy. The methodology proved successful; however, the results were highly dependent on the preparation of the solvents used to clean the samples after ...
Friedrich Bürger, Lienhard Wegewitz, Wolfgang Maus‐Friedrichs   +2 more
wiley   +1 more source

Associations between formal social support in early postpartum, parenting self-efficacy, and parent-infant bonding: A cross-sectional survey. [PDF]

Int J Nurs Stud Adv
Schobinger E, Lacroix A, Ramelet AS, Horsch A.   +3 more
europepmc   +1 more source

Influence of an Oxygen‐Free Atmosphere on Diamond‐Single‐Grain Scratching of Ti–6Al–4V

Advanced Engineering Materials, EarlyView.
Single‐grain scratching of Ti–6Al–4V is investigated under controlled, oxygen‐free, and ambient atmospheres using a novel experimental setup with in situ high‐speed imaging. The approach enables direct observation of chip formation and adhesion under suppressed oxidation.
Berend Denkena, Benjamin Bergmann, Michael Zenger   +2 more
wiley   +1 more source