High-Temperature Chemical Stability of Cr(III) Oxide Refractories in the Presence of Calcium Aluminate Cement. [PDF]
Materials (Basel), 2021 Xu T, Xu Y, Liao N, Li Y, Nath M.
europepmc +1 more source
Preparation Of Calcium Aluminate-Spinel Synthetic Aggregates Using Electrostatic Precipitated Dolomite DustAnd Calcined Alumina [PDF]
, 2012 Calcium alumniate-spinel phases have been developed for synthetic aggregate from ESP dolomite dust and calcined alumina. A huge amount of dolomite dust is collected at electrostatic precipitator (ESP) during dead burning of raw dolomite in Rotary Kiln ...
Kiche rai, Sanjeev
core
Physicochemical, Mineralogical, and Mechanical Properties of Calcium Aluminate Cement Concrete Exposed to Elevated Temperatures. [PDF]
Materials (Basel), 2021 Abolhasani A, Samali B, Aslani F.
europepmc +1 more source
The Effects of Prehydration on Cement Performance
, 2010 This study investigated the effects of cement prehydration on cement’s engineering properties. Anhydrous cement was exposed over a saturated KCl solution to maintain 85% RH, for 7 and 28 days.
Black, L +3 more
core
Calcium Sulfoaluminate Cement Clinkering [PDF]
, 2017 Non peer reviewedPublisher ...
Campbell Bannerman, Marcus Nigel +8 more
core
Steel Corrosion Behavior of Reinforced Calcium Aluminate Cement-Mineral Additions Modified Mortar. [PDF]
Materials (Basel), 2021 Wang Z +5 more
europepmc +1 more source
Discover SustainabilityThis study investigated the potential of liquid calcium aluminate cement (LCAC) as a sustainable substitute in the cement industry. The fluid form of LCAC effectively mitigates the rapid setting issues associated with traditional powdered calcium ...
Chia-Jung Tsai +4 more
doaj +1 more source
Electrical characterization of Calcium Aluminate (CA) in presence of chloride ions [PDF]
, 2015 International audienceChloride ingress is one of the major causes of reinforced concrete degradation. Chlorides accelerate the breaking of the protective layer of rebars favoring pitting corrosion; furthermore, corrosion products generate cracks in ...
Bastidas-Arteaga, Emilio +4 more
core +1 more source
Low cement high alumina castables: Effect of distribution coefficients [PDF]
, 2013 Refractory materials used in various areas of the iron and steel industry need to face severe challenges to meet critical operational parameters at high temperatures.
Parija, Anwesha
core