Corrosion-fatigue of additively manufactured Ti6Al4V. [PDF]
J Mech Behav Biomed MaterAdditive manufacturing (AM) has been used to process complex one-of-a-kind patient-specific implants, along with on-demand manufacturing with innovative geometries. AM parts are more susceptible to fatigue failure due to inherent porosities than conventionally processed parts.
Hogg WW +5 more
europepmc +4 more sources
Corrosion-fatigue lifetime of Aluminium–Copper–Lithium alloy 2050 in chloride solution
Materials & Design, 2015 The fatigue behaviour of Aluminium–Copper–Lithium 2050 alloy under two metallurgical states (T34 and T84) was studied in air for healthy and pre-corroded samples in a 0.7 NaCl solution. The results were compared to those obtained during fatigue–corrosion
M. Guérin +4 more
doaj +3 more sources
Corrosion Fatigue Crack Propagation Behaviour of a High Strength Low Alloy Steel in a Synthetic Sea Water Environment. [PDF]
, 1986 The corrosion fatigue crack propagation behaviour of a high strength low alloy steel, N-A-XTRA 70, in a synthetic sea water solution was tested using S. E. N. specimens subjected to a loading frequency of 0.1 Hz and a load ratio of 0.6.
Millar, Peter G.
core +7 more sources
Experimental and theoretical studies of corrosion fatigue in a high strength steel. [PDF]
, 1995 The present work consists of both experimental and theoretical aspects of corrosion fatigue in a high strength steel. Fatigue tests were conducted under fully reversed shear loading in an aerated 0.6M NaC1 solution at pH6, for a silico-manganese ...
Wu, Xiao Dong
core +6 more sources
A study of crack initiation in corrosion-fatigue of A.I.S.I 316 stainless steel by dynamic measurement of corrosion characteristics and corrosion current transients [PDF]
, 1980 This thesis was submitted for the degree of Doctor of Philosophy and awarded by Brunel University.A technique has been developed and applied to monitor corrosion current transients, in phase with a cyclic stress.
Martin, JW
core +7 more sources
In-situ corrosion fatigue performance and fracture mechanism of aviation aluminum alloy
Cailiao gongcheng, 2022 In order to study the fatigue properties of 2024 aluminum alloy under different corrosion fatigue conditions, First, an in-situ corrosion fatigue platform was established, and then non-corrosion fatigue test, pre-corrosion fatigue test and in-situ ...
WANG Fusheng +3 more
doaj +1 more source
Fatigue life prediction of gasoline storage tank considering varying current density and weld stress
Advances in Mechanical Engineering, 2022 In the field of corrosion fatigue crack research, how to couple corrosion and fatigue under various conditions is a problem worthy of discussion. According to the electrochemical corrosion principles and the superposition principles, studies have been ...
Genhua Yang +3 more
doaj +1 more source
Phenomenological investigation of the influence of Cathodic protection on corrosion fatigue crack propagation behaviour, in a BS 4360 50D type structural steel and associated weldment microstructures, in a marine environment. [PDF]
, 1984 The influence of Cathodic Protection potential upon corrosion fatigue crack propagation rates in a medium7strength ferritic-pearlitic structural steel (ES 4360 grade 50D) and associated weldment microstructures in simulated sea-water was studied and ...
Thompson, J. W. C.
core +7 more sources
Corrosion-Fatigue Analysis of High-Strength Steel Wire by Experiment and the Numerical Simulation
Metals, 2020 The paper takes the corrosion fatigue damage of cable or sling in the actual bridge as a starting point. The high-strength steel wire is chosen as the basic component to study the corrosion fatigue failure mode.
Songling Xue, Ruili Shen
doaj +1 more source
Management of Airframe In-Service Pitting Corrosion by Decoupling Fatigue and Environment
Corrosion and Materials Degradation, 2021 Corrosion-induced maintenance is a significant cost driver and availability degrader for aircraft structures. Although well-established analyses enable assessing the corrosion impact on structural integrity, this is not the case for fatigue nucleation ...
Loris Molent, Russell Wanhill
doaj +1 more source