Investigation on structure stability and damage mechanism of cemented paste backfill under the coupling effect of water-static load

Alexandria Engineering Journal
Cemented paste backfill (CPB) is easy to withstand the coupling effect of the mining operation equipment's crushing, water immersion, forming all kinds of intrinsic or extrinsic defects affecting its load-bearing capacity.
Zhiyi Liu, Deqing Gan, Haikuan Sun, Zhenlin Xue, Youzhi Zhang   +4 more
doaj   +1 more source

Study on the performance enhancement of biomedical implants: in vitro test under UV irradiation of titanium anodised in mixed electrolyte [PDF]

, 2018
Titanium (Ti) recently has widely been used in the biomedical applications due to its high performance. Therefore, surface modifications of titanium have attracted a lot of interest to provide better osseointegration.
Elfallah, Saleh S Saleh
core  

Corrosion and Process Analysis of a Preoxidized MgO Recyclate‐Based Cermet Anode in Laboratory‐Scale Na‐Cryolite Molten Salt Electrolysis of Aluminum at 1000°C

Advanced Engineering Materials, EarlyView.
EDX elemental map of the pre‐oxidized MgO–steel cermet anode cross section after electrolysis. The development of inert anodes for aluminum electrolysis remains challenging due to the high corrosivity of cryolite‐based melts at 950°C–1000°C. This study investigates the corrosion and process behavior of a carbon‐free MgO–steel cermet anode derived from ...
Alexander Adamczyk, Farhan Hossain, Felipe A. Garcia Paz, Serhii Yaroshevskyi, Felix Drechsler, Daniel Vogt, Christos G. Aneziris, Alexandros Charitos   +7 more
wiley   +1 more source

Occultation studies of planets and satellites: The occultation of epsilon Geminorum by Mars [PDF]

The occultation of epsilon Geminorum by Mars on 1976 April 8 was observed at three wavelengths and 4 ms time resolution with the 91 cm telescope. Temperature, pressure, and number density profiles of the Martian atmosphere were obtained for both the ...
Elliot, J. L., Sagan, C., Veverka, J.
core   +1 more source

Raman Spectroscopic Identification of Oxide Phases in a Corroded MgO–Steel Composite Anode Used in Aluminum Molten Salt Electrolysis

Advanced Engineering Materials, EarlyView.
Micro‐Raman spectroscopy is applied to characterize corrosion products in a recycled‐based MgO–316L steel composite anode after molten salt electrolysis. A depth‐dependent Fe–O/Fe–Al–O layer sequence of magnetite, hercynite, and an Al‐doped magnetite transition zone is identified.
Felix Drechsler, Serhii Yaroshevskyi, Alexander Adamczyk, Mahnaz Mehdizadehlima, Julia Richter, Cameliu Himcinschi, David Rafaja, Alexandros Charitos, Christos G. Aneziris, Jens Kortus   +9 more
wiley   +1 more source

Interaction of MgO Recyclate‐Based Cermet Anode With KF‐AlF3‐Al2O3 at 800°C During Laboratory Scale Aluminum Molten Salt Electrolysis

Advanced Engineering Materials, EarlyView.
A carbon‐free, as‐sintered MgO–steel cermet anode, fabricated via cold isostatic pressing using MgO–C refractory recyclate, was evaluated under laboratory‐scale K‐cryolite electrolysis at 800°C. Operation at this reduced temperature, combined with the electrolyte's limited electrical conductivity, led to an increase in cell voltage.
Farhan Hossain, Alexander Adamczyk, Felipe Alejandro Garcia Paz, Serhii Yaroshevskyi, Felix Drechsler, Daniel Vogt, Christos G. Aneziris, Alexandros Charitos   +7 more
wiley   +1 more source

SODIUM HYPOCHLORITE\u27S EFFECT ON NICKEL-TITANIUM ROTARY INSTRUMENTS AND ITS EFFECT ON RESISTANCE TO FRACTURE [PDF]

, 2007
The purpose of this study was to examine the effect of partial and total immersion in sodium hypochlorite on nickel-titanium rotary files and to determine whether resistance to fracture was influenced by the immersion time.
Smith, Michael Shane
core   +2 more sources

Interaction of Ladle Slag With Varying SiO2 Content and Recyclate‐Based MgO–C Refractories

Advanced Engineering Materials, EarlyView.
Ladle slags (CaO/Al2O3 = 1) with 1–20 wt% SiO2 were investigated in contact with industrial MgO–C refractories fabricated from fresh magnesia and 50 wt% recyclate. The sessile drop method at 1600°C reveals intensive gas formation, delayed slag infiltration in recyclate‐based samples, and, under high‐SiO2 slag, formation of a dense MgAl2O4‐rich ...
Anton Yehorov, Eldar Salpagarov, Anhelina Mospan, Till Manon Jannis Stadtmüller, Thomas Schemmel, Christos Georgios Aneziris, Olena Volkova   +6 more
wiley   +1 more source

Effect of NaCl Concentration on Galvanic Corrosion Behavior of Zinc and A1050 Couples

Electrochemistry
In this study, effects of NaCl concentration on galvanic corrosion behavior of zinc and A1050 couple was investigated by means of corrosion potential and galvanic current measurements, surface observation, electrochemical impedance measurements, and ...
Junho JANG, Azusa OOI, Eiji TADA
doaj   +1 more source

Impact of Sustainable Binders Based on Lignin and Collagen on the Volume Stability and Mechanical Properties of MgO‐C Refractories with MgO‐C Recyclates

Advanced Engineering Materials, EarlyView.
Collagen hydrolysate is evaluated as a sustainable binder for MgO‐C refractories. Its thermally induced cross‐linking and gas release lead to expansion and cracking in large bricks, but tailored batches with lignin, recyclates, or fine graphite improve the gas release while thermal treatment and stability.
Till M. J. Stadtmüller, Florian Kerber, Kirsten Moritz, Steffen Dudczig, Konstantin Kraushaar, Thomas Schemmel, Jana Hubálková, Patrick Gehre, Christos G. Aneziris   +8 more
wiley   +1 more source