Influence of Scan Strategies in Electron Beam Powder Bed Fusion on Solidification, Microstructure, and High‐Temperature Compressive Properties of γ′‐Strengthened Inconel 738LC

Advanced Engineering Materials, EarlyView.
Experiments and thermophysical simulations were conducted to investigate the electron beam powder bed fusion electron beam (PBF‐EB/M) process for the γ′‐strengthened nickel‐based superalloy Inconel 738LC. The results demonstrate the impact of process‐induced microstructural variations on high‐temperature mechanical behavior, providing a basis for ...
Jan Niklas Petenati, Karthik Kumar Banku, Prasanth Bondi, Ivan Zhirnov, Yangyiwei Yang, Gordon Schmidt, Jürgen Christen, Georg Hasemann, Manja Krüger, Bai‐Xiang Xu, Bilal Gökce, Silja‐Katharina Rittinghaus   +11 more
wiley   +1 more source

High‐Resolution Corrosion Fingerprinting of Alloy Libraries via Microdroplet Spectroelectrochemistry

Advanced Engineering Materials, EarlyView.
Ionic‐liquid microdroplet spectroelectrochemistry enables stable, localized electrochemical measurements over extended timescales. By coupling impedance spectroscopy, wetting analysis, finite‐element simulations, and operando Raman spectroscopy, it disentangles geometrical and electrochemical effects, opening new opportunities for rapid corrosion ...
Ekaterina Kurchavova, Oumaïma Gharbi, Mireille Turmine, Vincent Vivier   +3 more
wiley   +1 more source

Stress Disturbance Coefficient Method for Rock Burst Hazard Identification in Gully Regions: A Case Study

Applied Sciences
Gully topography significantly disturbs the in-situ stress field of underlying coal and rock masses, but the quantitative relationship between gully morphology and stress anomalies remains unclear.
Chao Zhou, Dazhao Song, Anliang Lu, Zhenlei Li, Aibing Jin, Shan Yin, Xueqiu He, Sitao Zhu, Menghan Wei, Taoping Zhong, Ping Wang   +10 more
doaj   +1 more source

OntOMat: Toward Ontology‐Based Product and Process Design Engineering and Optimization Solutions Fueling Circular Value Chains

Advanced Engineering Materials, EarlyView.
The OntOMat ontology establishes a structured framework for polymer matrix fiber reinforced composite materials, integrating manufacturing processes, characterization methods, and multiscale design through the VDI/VDE 3682 formalized process description standard.
Nicolas Christ, Jörg Hohe, Martin Kördel, Michael Giese, Niklas Toffert, Christian Seidel, Olaf Rehme, Patrik Schneider, Oliver Focke, Elie Abi Aoun, Claas Falldorf, Beñat Gutierrez, Alexandra Kühn, Sven Torstrick-von der Lieth, Christoph Herden, Erik Johannsen, Jan‐Uwe R. Schmidt, Felix Winkelmann, Andreas Schott, Daniel Schott   +19 more
wiley   +1 more source

A multiscale constitutive model for intergranular stress corrosion cracking in type 304 austenitic stainless steel [PDF]

, 2013
Intergranular stress corrosion cracking (IGSCC) is a fracture mechanism in sensitised austenitic stainless steels exposed to critical environments where the intergranular cracks extends along the network of connected susceptible grain boundaries.
Rahimi, S, Siddiq, A
core   +2 more sources

Characteristics of in-situ stresses and engineering stability analysis on the south section of the Bohai Strait Cross-Sea Corridor project

Dizhi lixue xuebao
Objective  The Bohai Strait Cross-Sea Corridor is an important maritime traffic project which joins the Liaodong and the Shandong peninsulas. The state of geostress is an important reference for engineering design and construction decision-making ...
QIAO Erwei, MA Xiumin, GUO Hualin, Sun Yao, JIANG Jingjie   +4 more
doaj   +1 more source

Impact of MgO Additions on the Oxidation Resistance and Compression Behavior of Vanadium Alloys

Advanced Engineering Materials, EarlyView.
An increase in oxidation resistance at 600 °C is achieved for alloys containing more than 2.5 wt.% MgO. It has been established that, along with V2O5, MgO6V2, and Mg2O7V2 are formed, which are presumed to enhance oxidative stability. Furthermore, the possible transformation of Mg‐vanadates through reaction with CO2, which presumably occurs in this ...
Ievgen Solodkyi, Mathias Galetz, Georg Hasemann, Fabian Lanoy, Emma White, Manja Krüger   +5 more
wiley   +1 more source

Enhancing Fatigue Crack Growth Resistance in Heterostructured Aluminum Bimetals by Tailored Interface Design

Advanced Engineering Materials, EarlyView.
Different Al/Al bimetals with a single engineered interface reveal how mechanical mismatch governs fatigue crack growth under cyclic loading. Additionally, loading–unloading–reloading tests link the microyielding behavior to the fatigue crack growth resistance, while crack‐path analysis reveals toughening mechanisms at the interface, highlighting ...
Sebastian Vollath, Philip Manuel Pohl, Heinz Werner Höppel   +2 more
wiley   +1 more source

Distinct Microstructural Characteristic Lengths Defining Notch Fatigue Crack Initiation and Propagation, and Defect Tolerance in Advanced Steels

Advanced Engineering Materials, EarlyView.
Schematic representation of modes of microcrack nucleation, growth and temporary arrestment at different boundaries, with the criteria for crack propagation in three scenarios: (1) large notch, (2) defect/small sharp notch, and (3) long crack. This work revisits and integrates results on the fatigue behavior of advanced bainitic steels (in particular ...
Lucia Morales‐Rivas
wiley   +1 more source

Editorial : In situ, revue de l’Inventaire général [PDF]

, 2012
Figure 1 Vierge à l’Enfant, statue en terre cuite entourée de François Lasa, photographe et de François Le Bœuf, chercheur, service régional de l’Inventaire en Pays-de-la-Loire Phot. Inv. F.
Verdier, Hélène
core