Vapor-etching honeycomb-like zinc plating layer for constructing anti-corrosion lubricant-infused surfaces

Frontiers in Chemistry, 2023
Introduction: Biomimetic lubricant-infused porous surfaces are developed and applied for omniphobicity and corrosion protection, which exhibit great advantages compared to superhydrophobic surfaces.Methods: Herein, superhydrophobic Fe@E-Zn@PFOA was ...
Xiaorui Song, Na Li, Zhongshan Wang, Shuangjian Li, Yuanyuan Hou   +4 more
doaj   +1 more source

Research status on preparation and properties of RE hafnates for thermal/environmental barrier coatings

Journal of Aeronautical Materials
The types，preparation methods，thermal and mechanical properties of rare earth hafnate materials and their corrosion behaviors exposed to low melting point silicate（CMAS） and high temperature water vapor are summarized.
SUN Zhipeng, REN Yutong, LIAO Guixiu, HE Ling, PAN Ling, ZHOU Wei, XIAO Peng, LI Yang   +7 more
doaj   +1 more source

Corrosion behavior of Si-18at%Y alloy in air/water-oxygen environment

Materials & Design
This work aimed to investigate the corrosion behavior of Si-18at%Y alloys in air oxidation and water-oxygen corrosion environments. The objective was to understand how different times, temperatures, and the presence or absence of water vapor affected the
Jingxin Li, Yongsheng Liu, Fang He, Fan Zhang, Binghui Zhang, Jing Wang, Yejie Cao, Nan Chai   +7 more
doaj   +1 more source

Latent Heat Flux Profiles from Collocated Airborne Water Vapor and Wind Lidars during IHOP_2002 [PDF]

, 2007
Latent heat flux profiles in the convective boundary layer (CBL) are obtained for the first time with the combination of the DLR water vapor differential absorption lidar (DIAL) and the NOAA high resolution Doppler wind lidar (HRDL).
Kiemle, Christoph, Fix, Andreas, Hardesty, Michael, LeMone, Margaret, Senff, Christoph, Brewer, Alan, Ehret, Gerhard, Poberaj, Gorazd, Wirth, Martin   +8 more
core   +1 more source

Influence of oxide films on primary water stress corrosion cracking initiation of alloy 600 [PDF]

, 2006
In the present study alloy 600 was tested in simulated pressurised water reactor (PWR) primary water, at 360 °C, under an hydrogen partial pressure of 30 kPa. These testing conditions correspond to the maximum sensitivity of alloy 600 to crack initiation.
Panter, J., Andrieu, Eric, Cloué, Jean-Marc, Foucault, M., Combrade, P., Viguier, Bernard, Cloué, J.M   +6 more
core   +1 more source

Natural gas dehydration by desiccant materials

Alexandria Engineering Journal, 2011
Water vapor in a natural gas stream can result in line plugging due to hydrate formation, reduction of line capacity due to collection of free water in the line, and increased risk of damage to the pipeline due to the corrosive effects of water ...
Hassan A.A. Farag, Mustafa Mohamed Ezzat, Hoda Amer, Adel William Nashed   +3 more
doaj   +1 more source

Cycling water vapor corrosion behavior and degradation mechanism of air plasma sprayed ytterbium silicate environmental barrier coatings

Cailiao gongcheng
Environmental barrier coatings （EBCs） are a key protective technology for the ceramic matrix composites （CMCs） hot end components of high-performance aircraft engines， which can significantly improve the service stability and reliability of the ...
KE Xijia, ZHOU Bangyang, REN Jiaqi, WANG Tianying, CUI Yongjing, WANG Changliang, GUO Mengqiu, JIAO Jian   +7 more
doaj   +1 more source

The FAC Experimental Research on Vapor-water Two-phase Flow Piping System of CAP1400 Secondary Loop

MATEC Web of Conferences, 2018
CAP1400 power plant is one of the advanced Third-generation Pressurized Water Reactor power plant. To ensure the safety and stability of the power plant secondary loop during operation, the corrosion characteristic of CAP1400 secondary loop should been ...
Zhai Shenhui, Pang Simin, Shao Jie, Zhu Hongqing, Zhang Xian, Liu Pengfei   +5 more
doaj   +1 more source

Horizontal structure function and vertical correlation analysis of mesoscale water vapor variability observed by airborne lidar [PDF]

, 2013
Analysis is presented of airborne lidar measurements of water vapor, covering a height range from 1.5 to 10.4 km, from three field campaigns (midlatitude summer, polar winter, and subtropical summer).
Kiemle, Christoph, L. Fischer, Fischer, Lucas, C. Kiemle, Craig, George C., G. C. Craig   +5 more
core   +1 more source

Oxidation behavior of SiCf/SiC composites prepared by melt infiltration process in water vapor corrosion environment

Cailiao gongcheng
The oxidation behavior of SiCf/SiC composites， fabricated through the melt infiltration process， is meticulously investigated in a water vapor corrosion environment. The findings reveal that after exposure to water vapor corrosion at 800 ℃ and 1200 ℃ for
AI Yingjun, ZHAO Chunling, LANG Xudong, SHU Xiaowen, YANG Jinhua, LIU Hu, ZHOU Yiran, JIAO Jian   +7 more
doaj   +1 more source