Characterization of Cracks and their Effects on the Effective Transport Pathways in Ni-YSZ Anodes after Reoxidation Using X-Ray Nanotomography

Reduction-oxidation cycling of Ni-based electrodes for solid oxide fuel/electrolysis cells irreversibly alters their microstructure and can cause the fracture of the electrolyte.
Cocco, A. P., Wang, S., Harris, W. M., Van herle, J., Wang, J., Cassenti, B. N., Nakajo, A., DeGostin, M. B., Greco, F., Peracchio, A. A., Deriy, A., Nelson, G. J., Chiu, W. K. S., Kiss, A. M., Chen-Wiegart, Y.   +14 more
core   +1 more source

Co-sintering of dense electrophoretically deposited YSZ films on porous NiO-YSZ substrates for SOFC applications [PDF]

, 2005
An original process for the preparation of YSZ dense films with a thickness lower than 10 μm over NiO-YSZ substrates is presented. This process involves the preparation of a green membrane of NiO-YSZ and subsequent electrophoretic deposition (EPD) of ...
Savo, G, Licoccia, S, Traversa, E, D'Epifanio, A, LICOCCIA, SILVIA, Rainer, A, SLicoccia, S, TRAVERSA, ENRICO, D'EPIFANIO, ALESSANDRA   +8 more
core  

LSM-YSZ Reactions in Different Atmospheres

, 2009
The influences of the oxygen partial pressure and the LSM/YSZ ratio on the LSM-YSZ interface reactions at 1,000 °C were investigated. Both pellets and diffusion couples were employed in the study.
Poulsen, Finn Willy, Chen, Ming, Liu, Yi-Lin, Y. ‐L. Liu, Hagen, Anke, F. W. Poulsen, M. Chen, P. V. Hendriksen, Hendriksen, Peter Vang, A. Hagen   +9 more
core   +1 more source

Preparation of Electrolyte Based on YSZ Material at the Green Boundary of NiO-YSZ

International Research Journal of Innovations in Engineering and Technology
The development of alternative energy technologies, particularly based on fuel cells, has become a primary focus in material research for energy applications. Solid Oxide Fuel Cells (SOFCs) are promising due to their high efficiency, fuel flexibility, and relatively low environmental impact.
Muhammad Faesal Febriandyono, null Sulistyo, Mohammad Tauviqirrahman, Rayhan Calista, Tatagraha Rahmanda, Fachrizal Radya Mahendra   +5 more
openaire   +1 more source

OsCPN10a, cooperating with OsCPN20 and OsHSP60‐3B negatively regulate ABA signaling and enhance seed storability in rice

Journal of Integrative Plant Biology, Volume 68, Issue 7, Page 2242-2263, July 2026.
Abscisic acid signaling homeostasis is essential for seed storability. The molecular chaperone OsCPN10a enhances rice seed storability by forming a trimeric chaperone complex with OsCPN20‐OsHSP60‐3B that attenuates abscisic acid signaling via direct interaction with OsPYL10‐OsABIL1, thereby maintaining starch integrity and offering a promising target ...
Sufeng Liao, Yidong Wei, Yongsheng Zhu, Kunyang Li, Ting Chen, Shuai Zhao, Fangxi Wu, Jinlan Wang, Pengbo Yu, Hongguang Xie, Liping Chen, Qiuhua Cai, Huaan Xie, Jianfu Zhang   +13 more
wiley   +1 more source

Pressurized Solid Oxide Fuel Cells: Operational Behavior

, 2011
The operational behavior of SOFC short stacks at elevated pressures up to 7 bar was examined. The experiments were performed on planar, anode-supported 5-cell short stacks.
Maier , Uwe, Willich, Caroline, Henke, Moritz, Leucht , Florian, Kallo , Josef, Westner, Christina, Friedrich , K. Andreas, Seidler , Stephanie   +7 more
core  

Physical and Electrical Properties of Yttria-Stabilized Zirconia Thin Films Prepared by Radio Frequency Magnetron Sputtering

Acta Polytechnica, 2013
This paper presents the electrophysical characteristics of a 7 mol.% yttria-stabilized zirconia (YSZ) thin film deposited by radio-frequency magnetron sputtering.
Dmitriy A. Golosov, Sergey M. Zavatskiy, Sergey N. Melnikov   +2 more
doaj  

Pengaruh komposisi dan variasi jumlah sapuan komposit YSZ-Al2O3 terhadap ketahanan termal dan kekuatan lekat pada YSZ/YSZ-AL2O3 double layer TBC untuk aplikasi nosel roket [PDF]

, 2015
TBC (Thermal Barrier Coating) dengan YSZ/Al2O3-YSZ top coat (TC) dan MCrAlY sebagai bond coat (BC) yang selanjutnya disebut sebagai YSZ/Al2O3-YSZ double layer TBC digunakan sebagai aplikasi material perintang panas pada dinding dalam nosel roket ...
Agustina, Ratna Tri
core  

Electrical conductivity of thick film YSZ

, 2019
When yttria-stabilized zirconia (YSZ) electrolyte is coated and co-sintered on top of Ni-YSZ anode support, the measured conductivities of YSZ thick films (10-30 mu m thick) are often lower than that of bulk YSZ.
Kwon, OH, Choi, GM
core   +1 more source

Improving high temperature corrosion resistance of Cr3C2–25NiCr coating by incorporating nano yttria-stablized zirconia

Discover Materials
The hot corrosion behavior of Cr3C2–25NiCr composite coatings reinforced with nano yttria stabilized zirconia (YSZ) was evaluated under actual boiler conditions in a thermal power plant at 850 °C with cyclic thermal loading.
Sukhjinder Singh, Khushdeep Goyal, Rakesh Bhatia   +2 more
doaj   +1 more source