Residual Life of Boiler Pressure Parts Made of the 13CrMo4-5 Steel after Long-Term Operation in a Creep Conditions [PDF]
Archives of Metallurgy and Materials, 2018 This paper presents the method for determination of the time of further safe service for welded joints of boiler components after exceeding the design work time.
A. Zieliński +5 more
doaj +4 more sources
Microstructure changes responsible for the degradation of the 10CrMo9-10 and 13CrMo4-5 steels during long-term operation [PDF]
Materials Research Express, 2019 The paper presents results of microstructure and mechanical testing examinations performed using optical and transmission electron microscopy, tensile tests and Charpy tests on 10CrMo9-10 and 13CrMo4-5 steels, before and after they were long-term ...
Monika Gwoździk +2 more
doaj +3 more sources
Characterization Of Oxide Layers Formed On 13CrMo4-5 Steel Operated For A Long Time At An Elevated Temperature [PDF]
Archives of Metallurgy and Materials, 2015 The paper contains results of studies into the formation of oxide layers on 13CrMo4-5 (15HM) steel long-term operated at an elevated temperature. The oxide layer was studied on a surface and a cross-section at the inner and outer surface of the tube wall.
Gwoździk M.
doaj +3 more sources
Temperature Resistance of Magnetoelastic Characteristics of 13CrMo4-5 Constructional Steel [PDF]
Acta Physica Polonica A, 2015 In the paper the results of investigation on tensile stresses dependence of magnetoelastic characteristics of cores made of 13CrMo4-5 constructional steel are presented. In the investigation step-cooling treated samples were used. The step-cooling process is a type of heat treatment simulating eects of passing time and environmental conditions ...
D. Jackiewicz +7 more
+8 more sources
QUANTITATIVE AND QUALITATIVE COMPARISONS BETWEEN NECESSARY METHODS, APPLICABLE TO WELDING STEEL 13CrMo4-5, TO ESTABLISH THE PREHEATING TEMPERATURE [PDF]
Fiabilitate şi Durabilitate, 2019 The paper presents and compares a series of standardized and non-standardized methods for determining the pre-heating temperature (Tpr) applied to reduce or eliminate negative effects resulting from the use of the welding process, such as cold cracking.
Dumitru Titi CICIC +3 more
doaj +2 more sources
Nonlinear fatigue life prediction model based on the theory of the S‐N fatigue damage envelope [PDF]
Fatigue &Fracture of Engineering Materials &Structures, Volume 45, Issue 5, Page 1480-1493, May 2022., 2022 Abstract A nonlinear model is proposed in light of the theory of isodamage curves, to assess the cumulative fatigue damage under multistage loading. The isodamage curves were developed through the theory of the S‐N fatigue damage envelope, proposed by Pavlou. The adopted functional form of the fatigue damage is a commonly accepted general form.
Fredrik Bjørheim +2 more
wiley +3 more sources
Plasma Transferred Arc (PTA) Cladding and TOPTIG Cladding of Tubes Made of Steel 13CrMo4-5
Biuletyn Instytutu Spawalnictwa, 2021 The article presents test results concerning the effect of a cladding method and technological process parameters on geometrical properties and dilution of overlay welds. Test overlay welds were deposited on tubes made of steel 13CrMo4-5. The chemical composition of the filler material used in the deposition process corresponded to that of alloy ...
Janusz Rykała, Maciej Różański
openaire +3 more sources
Journal of Achievements in Materials and Manufacturing Engineering, 2023 This paper presents a study aimed at determining the effect of the carburizing treatment process and the subsequent grinding process on the residual stresses occurring in ring-shaped specimens made of 13CrMo4-5 steel.During the tests, vacuum carburizing was used, achieving an effective case depth ECD = 0.5 mm.
R. Wójcik, J. Sawicki
openaire +2 more sources
Scientific Journal of Gdynia Maritime University, 2022 The paper presents a new technology for welding dissimilar steels using the TIG method. Following the welding, the joint was subjected to non-destructive testing, and subsequently a Vickers hardness measurement.
Agata Wieczorska, Tomasz Dyl
doaj +1 more source
Some advanced welding technologies applied for repair welding in power plants [PDF]
, 2021 Steels are subjected to many time-dependent degradation mechanisms when they are applied in electric power plants. They are exposed to high temperatures, multi-axial stresses, creep, fatigue, corrosion, and abrasion during such services. Used under these
Odanović, Zoran Dušan
core +2 more sources