Mapping erosion-corrosion of carbon steel in oil-water solutions : Effect of velocity and applied potential [PDF]
, 2012 In this study, the combined effects of erosion and corrosion on carbon steel were investigated in three environments containing crude oil, reservoir water, and a mixture of both solutions at a range of applied potentials, velocities and impact angle. The
Abdulrahman, Ghaith, Stack, Margaret
core +1 more source
Lubricants, 2022 The initiation of erosion and the coupled damage of erosion and corrosion on the surface of X65 pipeline steel with varying applied anodic currents were online monitored using the electrical resistance (ER) method.
Kongzhong Liu +5 more
doaj +1 more source
Some comments on mapping the combined effects of slurry concentration, impact velocity and electrochemical potential on the erosion–corrosion of WC/Co–Cr coatings [PDF]
, 2008 Materials exposed to aqueous slurry environments must not only resist the impact of solid particles and the flowing environment but also the degradation caused by electrochemical corrosion.
Abd El-Badia, T.M., Stack, M.M.
core +1 more source
Effect of the Heat Treatments on Corrosion and Erosion-Corrosion for Carbon Steel [PDF]
Engineering and Technology Journal, 2011 The aim of present work is to study the effect of different heat treatments [full annealing ,normalizing ,and hardening and tempering at (300C° ,600C°)] on general corrosion and erosion-corrosion for a carbon steel type (C35) in 3.5wt% NaCl solution as ...
Muna k.Abbass +2 more
doaj +1 more source
Low impact velocity wastage in FBCs : experimental results and comparison between abrasion and erosion theories [PDF]
, 2012 The use of technologies related to combustion of coal in fluidized bed combustors (FBCs) present attractive advantages over conventional pulverized coal units.
Almeraya-Calderón, F. +3 more
core +2 more sources
Use of Electrochemical Tests for Assessment of the Effect of Erosive Particle Size on the Erosion-Corrosion Behaviour of AISI 304L Austenitic Stainless Steel [PDF]
Materials Research, 2016 The degradation of AISI 304L stainless steel under static corrosion, liquid impingement and corrosion-erosion was studied using polarization curves. Static corrosion and liquid impingement tests were performed in 3.5% NaCl solution.
Diana Maria López +2 more
doaj +1 more source
Investigation of Erosion-corrosion of Carbon Steel Elbow in 3.5% Sodium Chloride Containing Quartz
International Journal of Electrochemical Science, 2022 In this study, the erosion-corrosion (E-C) behavior at different locations of a 90° horizontal elbow was investigated under the condition of liquid-solid two-phase flow by weight loss measurement, electrochemical measurement and surface analysis through ...
Zongwu Hu, Rui Xing, Jianguo Liu
doaj +1 more source
Journal of Materials Research and TechnologyAging hardening nickel-based alloy 718 is a key material for oil and gas applications, but it is susceptible to fatigue failure under the combined effects of cyclic loading and corrosive media. This study focused on exploring low-temperature Arc-Enhanced
Rongrong Chen +8 more
doaj +1 more source
Flow accelerated corrosion and erosion−corrosion behavior of marine carbon steel in natural seawater
npj Materials Degradation, 2021 In this work, flow accelerated corrosion (FAC) and erosion−corrosion of marine carbon steel in natural seawater were electrochemically studied using a submerged impingement jet system. Results show that the formation of a relatively compact rust layer in
Yunze Xu +6 more
doaj +1 more source
Metals, 2021 In this paper, a pragmatic technique has been developed to evaluate the erosion-corrosion behavior of three kinds of ZrN coatings (i.e., monolayer, multilayer, and gradient layers) which were deposited on AISI 420 martensitic stainless steel using an ion-
Yuntao Xi +7 more
doaj +1 more source