Results 41 to 50 of about 5,804 (225)
Literature review on fractography of dental ceramics
, 2022 치과용 세라믹의 파절실험 후 파절이 발생한 원인을 분석하면 세라믹의 임상적용 가능성을 높일 수 있다. 파절원인을 파악하기 위한 파단면분석은 주사전자현미경 등 영상기술의 발달로 점차 널리 적용되고 있는데 이를 정확히 해석하기 위해서는 실험조건 설정이 중요하다. 파절시편이 오염되지 않도록 보관하고 세척하며, 관찰을 위해 금속 전처리가 필요하다.
Chan-Jin Park +5 more
core +1 more source
Study of fractography of ferritic ductile iron at different temperatures and loading conditions
Materials Research ExpressThis study characterizes the fractography of ferritic ductile iron under various loads, including tensile, fatigue and bending, and impact conditions. The results indicate that ductile fracture is the primary mechanism observed during tensile testing at ...
Wenjie Wang +9 more
doaj +1 more source
Influence of Test Temperature and Test Frequency on Fatigue Life of Aluminum Alloy EN AW‐2618A
Advanced Engineering Materials, EarlyView.The influence of test temperature and test frequency on the fatigue life of EN AW‐2618A is investigated. High‐cycle fatigue tests are performed at different test temperatures and frequencies on the 1000 h/230°C overaged state. Both test parameters reduce fatigue life due to time‐dependent damage mechanisms.
Ying Han +5 more
wiley +1 more source
Nondestructive Testing of Welded Composite Metal Foams
Advanced Engineering Materials, EarlyView.X‐ray computed tomography (CT) is used to evaluate welded steel–steel composite metal foam (CMF) joints of two density classes. It reports variation in postweld spatial void distribution and correlates it to weld‐induced changes, mechanical performance, and failure within welded CMF panels.
Chinmaya Prerana Inguva +2 more
wiley +1 more source
Microscopic observation of creep-fatigue crack propagation in lead-free solder
Nihon Kikai Gakkai ronbunshu, 2015 Creep-fatigue crack propagation tests of lead-free solder were conducted under various loading waveforms. The waveforms adapted in displacement-controlled tests were four triangular waveforms: pp waveform having fast loading-unloading, cc waveform having
Keisuke TANAKA +4 more
doaj +1 more source
Advanced Science, EarlyView.A quasi‐periodic Dart‐Kite (QDK) metastructure with a golden‐ratio‐constrained strong–weak bond network simultaneously enhances strength, toughness, and damage tolerance. Its distributed topology enables predictable, tailorable crack paths for precise fracture control and stable mechanics, demonstrating a high‐performance, controllable architecture ...
Tianyu Gao +3 more
wiley +1 more source
International Journal of Mining Science and Technology, 2022 Ultrasonic fracturing (UF) can be used to form crack networks for oil or gas in the mining industry and hard rock excavation. In this paper, the three-dimensional internal laser-engraved crack method (3D-ILC) is introduced to make penny-shaped internal ...
Haijun Wang +4 more
doaj +1 more source
Failure Investigation of Alloy 625 Sockolets After Prolonged Service in an Ammonia Cracker Unit
Materials and Corrosion, EarlyView.The failure of the sockolets was caused by intergranular cracking and fracture. The thick and highly brittle nitrided layer formed intergranular surface cracks, which propagated along grain boundaries into the base alloy substrate due to the presence of brittle Cr‐rich carbides. ABSTRACT Several sockolets of Alloy 625 operating at 540°C in contact with
Kamlesh Chandra +2 more
wiley +1 more source
Polymer Composites, EarlyView.Comparison of powder impregnation and hybrid commingled non‐wovens for PA6/rCF nonwoven composites. The two‐step powder route gives lower voids and higher properties, while the single‐step hybrid route is limited by precursor inhomogeneity and high void content.
Gaia Francesca Lupia +4 more
wiley +1 more source