Experimental investigation on the fatigue and fracture properties of a fine pearlitic rail steel
Fracture and Structural IntegrityThis study reports an experimental investigation of the fatigue and fracture resistance of R350HT, a heat-treated pearlitic rail steel with refined microstructure used in rails.
Davide Leonetti, Bart Schotsman
doaj +3 more sources
, 1901 This is a report of the employees of the Bethlehem Steel Company, along with wages and salaries from 1901. The report provides statistical data about the employees at the Bethlehem Steel, specifically detailing the number of workers employed per "class ...
core
Strain Aging of Heavily Drawn Pearlitic Steel Wires
, 2007 The strain aging of heavily drawn pearlitic steel wires has been studied by means of electrical resistivity mearsurement. The kinetic of the early stage of strain aging after being drawn to true strain 2.89 is described by a Johnson-Mehl equation.
Jin, X., Min, N., Gu, Yijia
core +1 more source
Analysis of the Degradation of Pearlitic Steel Mechanical Properties Depending on the Stability of the Structural Phases. [PDF]
Materials (Basel), 2023 Šmak R +5 more
europepmc +1 more source
Effect of hydrogen embrittlement on the microstructures of electroplated steel alloy 4130
Ain Shams Engineering Journal, 2018 In this work, the behavior of hydrogen embrittlement and corrosion of nickel, cadmium and copper electroplating steel alloy 4130 were examined. The microstructures of exposed steel 4130 characterized by energy dispersive spectroscopy (EDS) and scanning ...
Y. Reda, A.M. El-Shamy, Ashraf K. Eessaa
doaj +1 more source
Teshugang, 2007 The evolution of structure of 0. 78C-1. 03Cr eutectoid pearlitic steel Φ8 mm x 45 mm sample with two pass equal channel angular pressing at ambient temperature has been studied by scanning, transmission electron microscope and X- ray diffraction method ...
赵军 +4 more
doaj
Friction between pearlitic steel surfaces
, 2018 Experiments rubbing two pearlitic rail steel surfaces against each other were done using an axial-torsion test rig. After the experiments were completed, the surfaces were observed under stereomicroscope, and the wear debris were examined. The aim of the
Ahlström, Johan,, Jessop, Casey,
core
INFLUENCE OF DEFORMATION IN THE LINE OF WIRE MILL 150 ON DISPERSION OF PEARLITE OF STEEL 80K
Литьë и металлургия, 2014 Peculiarities of formation and distribution of pearlitic structure of steel 80K in a blank and after deformation in various areas of wire mill (in semi-finished rolled products and rolled wire) are established.
V. A. Lutsenko +4 more
doaj
On the modeling of anisotropy in pearlitic steel subjected to rolling contact fatigue [PDF]
, 2012 One of the main sources of damage caused by Rolling Contact Fatigue (RCF) in railway components is the large plastic deformations that accumulate in the surface layer of these components.
Larijani, Nasim
core
Crack tip fields and mixed mode fracture behaviour of progressively drawn pearlitic steel
Fracture and Structural Integrity, 2015 This paper deals with the influence of the cold drawing process on the fracture behaviour of pearlitic steels. To this end, fracture tests under axial loading were performed on steel wires with different drawing degree (from a hot rolled bar to a ...
J. Toribio, B. González, J.C. Matos
doaj