Results 41 to 50 of about 573 (225)

Thermomechanical Fatigue and Creep–Fatigue Interaction of Inconel 718 Additively Manufactured by Laser Beam Powder Bed Fusion

Advanced Engineering Materials, EarlyView.
Thermomechanical fatigue tests of laser beam powder bed fusion (PBF‐LB) Inconel 718 show that the additively manufactured material reaches almost the lifetimes of conventionally‐rolled material under no‐dwell conditions. Introducing dwell times at the maximum temperature markedly reduces the lifetimes due to pronounced grain boundary sliding associated
Stefan Guth, Tomáš Babinský, Jan Lars Riedel, Wen Hao Kan, Aijun Huang, Martin Heilmaier, Ivo Šulák   +6 more
wiley   +1 more source

Numerical Simulation of the Effect of Pre-Strain on Fatigue Crack Growth in AA2024-T351

Metals
The objective here is to study the effect of pre-strain on fatigue crack growth (FCG) in 2024-T351 aluminum alloy. Three pre-strain conditions were considered: without pre-strain, compressive and tensile permanent pre-strains of 4%.
Diogo M. Neto, Edmundo Sérgio, André Agra, Fernando V. Antunes   +3 more
doaj   +1 more source

Karl Popper and the Mechanisms of Hydrogen Embrittlement

Advanced Engineering Materials, EarlyView.
Representation of the beginning of loss of ductility rather than embrittlement. Small concentrations of hydrogen in a diffusible form within iron are well‐established to harm the mechanical integrity of steels. There are theories that attempt to explain the pernicious role of hydrogen.
H. K. D. H. Bhadeshia
wiley   +1 more source

Modeling of creep-fatigue interaction effects on crack growth at elevated temperatures

MATEC Web of Conferences, 2018
The well-known load frequency effect on creep-fatigue crack growth is explained by the interactions between fatigue and creep loading and is quantified using the concept of plasticity-induced crack closure.
Potirniche Gabriel P.
doaj   +1 more source

Microstructure‐Controlled Crack Propagation and Fracture Resistance in MoSiBTiC Alloy Revealed by Multiscale Extended Finite Element Method Modeling

Advanced Engineering Materials, EarlyView.
A two‐dimensional multiscale finite element analysis framework was established for the first‐generation MoSiBTiC alloy, and the mechanical and fracture‐related parameters of the constituent phases were calibrated through experiments and simulations. The framework provides a basis for analyzing crack propagation behavior in its complex microstructure ...
Junfeng Du, Takahiro Kaneko, Xinyu Yan, Takahito Ohmura, Kyosuke Yoshimi   +4 more
wiley   +1 more source

Microstructure Evolution of a VMnFeCoNi High‐Entropy Alloy After Synthesis, Swaging, and Annealing

Advanced Engineering Materials, EarlyView.
The synthesis and processing (rotary swaging and annealing) of the novel VMnFeCoNi alloy is investigated, alongside the estimation of the grain size effect on hardness. Analysis of a wide grain size range of recrystallized microstructures (12–210 µm) reveals a low annealing twin density.
Aditya Srinivasan Tirunilai, Zeki Ayrildi, Buse Şen, Maik Rajkowski, Mathias Redondo Garcia, Markus Stricker, Guillaume Laplanche   +6 more
wiley   +1 more source

Slip Localization Intensification Mediated by Grain Boundary Sliding in a Polycrystalline Nickel‐Based Superalloy

Advanced Engineering Materials, EarlyView.
The temperature dependence of fatigue behavior in nickel‐based superalloys is investigated through high‐resolution measurements of plastic localization. While increasing temperature reduces localization and enhances fatigue performance in René 88DT, Inconel 718 exhibits a sharp degradation at intermediate temperature due to intensified slip ...
M. Calvat, D. Anjaria, I. Woo, C. Bean, D. Texier, J. C. Stinville   +5 more
wiley   +1 more source

Fatigue Crack Initiation and Growth in Nanocrystalline Ni at Multiple Length‐Scales

Advanced Engineering Materials, EarlyView.
Overview of miniaturized in situ SEM fatigue setup and resultant fatigue crack growth data for nanocrystalline Ni. The presented study focuses on the analysis of fatigue crack growth rate (FCGR) in focused ion beam‐notched microcantilevers prepared from nanocrystalline (NC) Ni as a model material.
Igor Moravcik, Alexander Jelinek, Markus Alfreider, Jutta Luksch, Anton Hohenwarter, Florian Schaefer, Christian Motz, Daniel Kiener   +7 more
wiley   +1 more source

Influence of Test Temperature and Test Frequency on Fatigue Life of Aluminum Alloy EN AW‐2618A

Advanced Engineering Materials, EarlyView.
The influence of test temperature and test frequency on the fatigue life of EN AW‐2618A is investigated. High‐cycle fatigue tests are performed at different test temperatures and frequencies on the 1000 h/230°C overaged state. Both test parameters reduce fatigue life due to time‐dependent damage mechanisms.
Ying Han, Julian M. Rosalie, Jan Radners, Mauro Madia, Philipp von Hartrott, Birgit Skrotzki   +5 more
wiley   +1 more source

Experimental Characterization and Constitutive Modeling of the Effect of Prior Inelastic Strain on the Viscoplastic Behavior of AD730 at 700 °C

Advanced Engineering Materials, EarlyView.
This study shows that superalloys used in aircraft engine disks become much more prone to deformation at high temperatures if they have been strained during manufacturing. This effect increases with the level of prior strain but eventually reaches a limit.
Fabio Machado Alves da Fonseca, Patrick Villechaise, Malik Durand, Arnaud Longuet, Florent Coudon, Loïc Signor, Julien De Jaeger, Dominique Eyidi, Nathalie Bozzolo, Jonathan Cormier   +9 more
wiley   +1 more source