Study on Stress Corrosion Susceptibility of High Manganese Austenitic Cryogenic Steel HM400 in Liquid Ammonia Medium [PDF]
Cailiao Baohu, 2023 For studying the stress corrosion susceptibility of high manganese austenitic cryogenic steel HM400 in liquid ammonia medium, the slow strain rate test (SSRT) was used to investigate the stress corrosion susceptibility of high manganese austenitic ...
HU Pan, KONG Wei-hai, ZHANG Qiang, WU Zhi-gang, LIU Yan
doaj +1 more source
International Journal of Electrochemical Science, 2019 In this study, the hydrogen embrittlement behavior of an ultrahigh strength mooring chain steel with a tensile strength of 1150 MPa was evaluated. The hydrogen was precharged into the notched specimen by electrochemical hydrogen charging.
Songjie Li +4 more
doaj +1 more source
Energy dissipation mechanism and damage model of marble failure under two stress paths [PDF]
Fracture and Structural Integrity, 2014 Marble conventional triaxial loading and unloading failure testing research is carried out to analyze the elastic strain energy and dissipated strain energy evolutionary characteristics of the marble deformation process.
Liming Zhang +3 more
doaj +2 more sources
International Journal of Electrochemical Science, 2018 In this study, SUS 304 stainless steel was cold rolled with various degrees of rolling reduction. The microstructure and stress corrosion cracking behavior before and after cold rolling were investigated.
Shanlin He, Daming Jiang
doaj +1 more source
Effect of pH on Stress Corrosion Cracking of 6082 Al Alloy
Metals, 2018 In this work, the effect of pH (3, 7 and 10) on the stress corrosion cracking behavior of 6082 aluminum alloy, in a 0.3 M sodium chloride (NaCl) aqueous based solution was investigated.
C. N. Panagopoulos +3 more
doaj +1 more source
International Journal of Electrochemical Science, 2014 The effect of electrochemical potential and chloride concentration on stress corrosion cracking (SCC) behavior of 23Co14Ni12Cr3Mo ultra-High strength steel were investigated by using slow strain rate technique (SSRT).
Jianhua Liu +4 more
doaj +1 more source
Investigation on the Property Degradation of Nickel-Base Alloy 825 in High Pressure H2S Environments
International Journal of Electrochemical Science, 2012 The effects of tensile rate and H2S pressure on the tensile property of nickel-base alloy 825 in wet H2S environments were investigated by the slow strain rate tensile test (SSRT) and scanning electron microscopy (SEM).
S.Q. Zheng +4 more
doaj +1 more source
Gong-kuang zidonghua, 2023 At present, the correlation analysis between the acoustic emission characteristics of the rock failure process and the fractal characteristics of sample fragments has been carried out. Some achievements have been obtained.
LYU Pengfei +3 more
doaj +1 more source
Archives of Metallurgy and Materials, 2015 The potentiodynamic polarization test and slow strain rate tensile tests of X80 pipeline steel were performed in 0.5M Na2CO3-1M NaHCO3 solution to study the electrochemical and stress corrosion cracking properties.
Zhao W., Zou Y., Xia D.X., Zou Z.D.
doaj +1 more source