Anodic oxidation and stress corrosion cracking (SCC) of titanium alloys

Journal of Materials Science, 1973
Uniform and reproducible oxide films were formed on alloy Ti-6AI-6V-2.5Sn by anodic oxidation in aqueous 0.5~ H3BO3, at 10 mA cm -2 and voltages up to 110V; dielectric break down occurred above 120V. A parallelism was found between the effect of environmental factors on stress corrosion cracking (SCC), as reported in the literature and the anodic ...
A. Aladjem, M. Aucouturier, P. Lacombe
openaire   +1 more source

Testing and evaluation methods for stress corrosion cracking (SCC) in metals

2011
The development of standardised methods of testing is a key element in the prevention of stress corrosion cracking (SCC) in order to provide a unified reference framework. A range of test methods is available in the form of international and national standards and procedures, comprising a wide variety of test methods for assessing SCC and also a ...
Dietzel, W., Bala Srinivasan, P., Atrens, A.   +2 more
openaire   +4 more sources

Stress corrosion cracking (SCC) of copper and copper-based alloys

2011
This chapter summarizes stress corrosion cracking of copper and copper-based alloys in different chemical, thermal, and electrochemical environments. The chapter begins with description of different copper-based alloys and their common application. A description of different operating SCC mechanisms for the copper-based alloys is provided.
Kannan, M. Bobby, Shukla, P.K.
openaire   +1 more source

Stress Corrosion Cracking (SCC) and Corrosion Fatigue Cracking (CFC) of a Duplex Stainless Steel in White Water Environments

CORROSION 2003, 2003
Abstract The present article addresses the stress corrosion cracking (SCC) and subsequent corrosion fatigue cracking (CFC) behavior of a heat-treated duplex stainless steel (DSS) in paper-machine white waters containing chloride and thiosulfate ions.
J.J. Perdomo, P.M. Singh, J. Mahmood, J.E. Oteng   +3 more
openaire   +1 more source

PR-261-103605-R01 Investigation on the Dormancy of Stress Corrosion Cracking (SCC) Cracks

2013
The objectives of this research were to investigate SCC dormancy and re-activation behavior in term of 1) effect of low frequency (= 10-5 Hz) and cyclic stress typical of pressure fluctuation (R = 0.8) and 2) the inhibitive effect of organics on the growth rate of SCC cracks.
null Xie, null Yazdanfar, null Given
openaire   +1 more source

Experimental and theoretical investigation of stress corrosion crack (SCC) growth of polyethylene pipes

Polymer Degradation and Stability, 2009
Degradation of polymers is usually manifested in a reduction of molecular weight, increase of crystallinity in semicrystalline polymers, increase of material density, a subtle increase in yield strength, and a dramatic reduction in toughness. Stress corrosion cracking (SCC) results from strongly coupled thermo-mechano-chemical processes, and is ...
Byoung-Ho Choi, Alexander Chudnovsky, Rajesh Paradkar, William Michie, Zhenwen Zhou, Pak-Meng Cham   +5 more
openaire   +1 more source

Stress Corrosion Cracking (SCC) Management Program for Onshore Pipelines

Volume 2B: Pipeline and Facilities Integrity
Abstract Stress Corrosion Cracking (SCC) on buried pipelines results from simultaneous presence of tensile stress, corrosive environment, and material that is susceptible to SCC. In-Line-Inspection (ILI) using smart tools have been effective in the industry for locating and sizing SCC on pipelines.
Nauman Tehsin, Mohammed A. Al-Rabeeah, Abdullah S. Alghamdi, Murtadah A. Al-Hashem, Mohammed F. Aljama   +4 more
openaire   +1 more source

STRESS CORROSION CRACKING (SCC) OF LOW CARBON STEEL IN SELECTED ENVIRONMENTS

Journal of Metallurgy and Materials Engineering
This study has investigated the effect of various values of tensile stress on low carbon steel in different environments (1MH2SO4, 1MHCl, 1MNaOH and H2O) where most conventional mild steels are normally exposed to while in service. The mild steel samples were pre-weighed and tensed in each of the environments with different stress values of 126.8N/m2 ...
S. E. Ede, B.A. Okorie, A.O. Agbo
openaire   +1 more source

Enhancements in Susceptibility of Stress Corrosion Cracking (SCC) on Liquid and Gas Pipelines

Volume 2B: Pipeline and Facilities Integrity
Abstract Saudi Aramco is a fully integrated, global petroleum enterprise and a world leader in exploration, production, refining, transportation, distribution, shipping and marketing. The company runs a vast network of vintage pipelines from pre-1979 period to transport oil, gas and refined products all over the Kingdom of Saudi Arabia ...
Nauman Tehsin, Mohammed A. Al-Rabeeah, Abdullah S. Alghamdi, Yaseen A. Abduljawad, Ahmad R. Al-Saif   +4 more
openaire   +1 more source

ChemInform Abstract: Stress Corrosion Cracking (SCC) of Admiralty Brass in Sulphate Solutions.

Chemischer Informationsdienst, 1986
AbstractThe SCC of Admiralty brass exposed, under open circuit conditions, to Na2SO4‐ Cu‐ S04 solutions has been investigated as a function of acidity and Cu" concentration, by means of ′U′‐bend and of constant load tests.
openaire   +1 more source