Results 1 to 10 of about 271 (103)
Fenmo yejin jishu, 2022 通过固体火箭发动机地面热试车实验获得烧蚀后的钼镧喷管试样，对比分析了烧蚀前后试样的金相组织，在常温和1000 ℃条件下进行了钼镧材料的力学性能实验。结果表明：对于工作时间2.1 s的固体火箭发动机中搭载使用的钼镧喷管，内型面形状完整，尺寸无明显变化，抗烧蚀性能表现良好；烧蚀前后金相组织对比显示晶粒发生再结晶，特别是喷口及喷管中部工作温度高的位置，形貌变化明显，由细长的纤维状变为等轴晶趋势。镧的氧化物粒子对钼起到了韧化作用，合金试样1000 ℃高温和常温下断口出现颈缩和韧窝，高温下韧窝深浅差异更大 ...
林冰涛 +6 more
doaj +1 more source
气孔和晶粒尺寸不均匀系数对方波脉冲大电流作用下高电位梯度氧化锌陶瓷失效的影响
Dianci bileiqi, 2021 氧化锌电阻片在脉冲大电流作用下可能失效,威胁着电力设备及电力系统安全稳定运行。脉冲大电流作用下,电阻片瓷体的失效形式主要源自于瓷体本身的穿孔和炸裂。显微形貌观测结果表明,穿孔通道处有显著的晶粒熔融痕迹和微裂纹,这说明穿孔通道起源于电阻片电流、焦耳热局部集中,导致瓷体熔融和炸裂。基于未破坏区域和穿孔通道区域的微观分析,首次定义了晶粒尺寸分布的不均匀系数,统计分析了气孔及晶粒尺寸分布。计算结果表明,氧化锌电阻片穿孔通道附近气孔含量较多,且晶粒分布更加不均匀 ...
王瑶 +9 more
doaj
Size effect on crystallite microstructure in nanocrystalline brookite-based TiO2(纳米板钛矿基TiO2的晶粒尺寸效应)
Zhejiang Daxue xuebao. Lixue ban, 2001 借助精确的X射线衍射测量，结合独立衍射峰对不同晶粒度纳米板钛矿基TiO2样品中板钛矿和金红石相的微结构参量进行了较细致的研究，给出了标征物相、晶面指数(hk1)和晶面间距dhkl值，详细分析结果的系列XRD谱，并得到晶面间距、晶格常数、轴比、晶胞体积等参数数值及其相对常规粗晶的变化情况，从而初步揭示出其晶粒微结构的尺寸效应.作者首次发现，纳米板钛矿基TiO2样品中板钛矿和金红石相晶粒均存在着非单调的各向异性晶格畸变.
LIUXiang-dong(刘向东) +4 more
doaj +1 more source
Dianci bileiqi, 2022 作为重要的过电压防护元件,ZnO压敏电阻片的性能也需要不断提高。对ZnO压敏电阻片制备工艺中聚乙烯醇(PVA)的影响进行了研究。通过对比不同PVA种类及含量对造粒的影响后发现,选用的PVA聚合度越高,烧结陶瓷的晶粒尺寸就越小;PVA的添加量越多,晶粒尺寸也越小;其次PVA的聚合度会影响到压敏陶瓷的晶界电阻和击穿场强,它们之间成正相关的趋势,但是过量添加PVA会导致其晶界电阻活化能减小,压敏特性降低,导致泄漏电流密度增大;采用低聚合度的PVA会改善电气性能,即提升其压敏特性并降低泄漏电流密度;造粒过程中 ...
张兆华 +9 more
doaj
Rare Metals, EarlyView.ABSTRACT Nanocomposite permanent magnets with reduced rare‐earth content represent a promising class of materials for next‐generation high‐performance applications. However, asynchronous precipitation of soft and hard magnetic phases often results in grain size mismatch and limited coercivity.
Xiaowei Zhang +6 more
wiley +1 more source
Rare Metals, EarlyView.ABSTRACT The evolution of the γ′−Ni3(Al, Ti) phase in superalloys is governed by a coupled coalescence‐ripening mechanism driven by elemental diffusion. In this study, thermal exposure experiments were performed at 750°C and 800°C for durations ranging from 100 to 20,000 h.
Zhaotian Wang +5 more
wiley +1 more source
Rare Metals, Volume 45, Issue 1, January 2026.ABSTRACT TA18 alloy is an ideal material for piping systems in the aerospace field, the low notch sensitivity and high damage tolerance enhance its engineering application value. However, the complex failure mechanism influenced by strain gradient necessitates further improvement of the service stability for TA18 alloy in practical engineering ...
Xin Du +6 more
wiley +1 more source
Yttrium Addition Co‐Enhances the Plasticity and Corrosion Resistance of TiB2‐Refined Al‐Mg‐Zn Alloys
Rare Metals, Volume 45, Issue 1, January 2026.ABSTRACT To address the degradation of corrosion resistance induced by Al‐5Ti‐B grain refiner during the strengthening of Al‐Mg‐Zn alloys, this study innovatively employed a rare earth element yttrium (Y) alloying strategy to achieve synergistic enhancement of mechanical strength and corrosion resistance.
Wen‐Tao Qin +9 more
wiley +1 more source
稀土氧化物对ZnO-Bi2O3系压敏陶瓷晶粒分布及电气性能的影响
Dianci bileiqi, 2008 研究了稀土氧化物Ce2O3、Gd2O3、La2O3、Y2O3对ZnO-Bi2O3系压敏陶瓷晶粒尺寸和电气性能的影响,结果表明,稀土氧化物可有效地抑制ZnO晶粒的生长,掺杂Ce2O3、Gd2O3、La2O3、Y2O3后,晶粒的主要分布分别为0～18μm、0～14μm、0～11μm、0～16μm;平均晶粒尺寸下降,其中掺杂Gd2O3后晶粒尺寸最小,为6.2μm。ZnO晶粒分布的标准方差明显下降,改善了晶粒尺寸分布的均匀性。掺杂稀土氧化物后,电位梯度显著提高,E1mA达到了427.5V/mm ...
李盛涛, 成鹏飞, 王玉平, 朱斌
doaj
Dianci bileiqi, 2013 ZnO压敏陶瓷击穿场强E1mA由晶粒尺寸和单个晶界击穿电压两个因素共同决定,沿用之前提出的微观结构模型,在晶粒尺寸一定,晶界电压服从正态分布;晶界电压一定,晶粒尺寸服从正态分布;和晶粒尺寸、晶界电压都服从正态分布三种条件下,用Matlab分别模拟击穿场强随厚度的变化关系,结果表明ZnO压敏陶瓷击穿场强的几何效应主要来自晶粒尺寸和分布的影响。在此基础上,对初始厚度不同的试样进行击穿场强与厚度的关系模拟,从结果可以看到,无论是高击穿场强还是低击穿场强的试样,都存在几何效应。
鲍婕, 王政留, 李盛涛
doaj