Influence of choked angle of bearing channel on profile grain structure during multi-hole extrusion of aluminum alloy [PDF]
, 2018 Direct extrusion of aluminum alloy EN AW-6060 was carried out applying a four-hole die with pair-wise parallel and choked long channels. Due to the dissimilar friction inside parallel and choked channels profiles with different length were extruded ...
Müller, Sören, Sanabria, Vidal
core +1 more source
Microstructure evolution and flow stress modeling of SA508Gr.4N steel during hot deformation process
Cailiao gongcheng, 2021 The isothermal deformation behavior of Ni-Cr-Mo low alloy SA508Gr.4N steel at deformation temperature of 850-1200 ℃, strain rate of 0.001-1 s-1, and true strain of 0.9 was studied by using Gleeble-1500D thermal simulation testing machine.The physically ...
QIAO Shi-bin +4 more
doaj +1 more source
Flow stress and hot deformation activation energy of 6082 aluminium alloy influenced by initial structural state [PDF]
, 2019 Stress-strain curves of the EN AW 6082 aluminium alloy with 1.2 Si-0.51 Mg-0.75 Mn (wt.%) were determined by the uniaxial compression tests at temperatures of 450-550 degrees C with a strain rate of 0.5-10 s(-1).
Kawulok, Petr +5 more
core +1 more source
iScience, 2022 Summary: Bulk aluminum rarely forms deformation or annealing twins owing to its high stacking fault energy. We report a novel twinning mechanism mediated by dynamic recrystallization in 6N pure aluminum under high strain rate (∼1.3 × 104 s−1) impact at a
Mao Liu +6 more
doaj +1 more source
Dynamic recrystallization analysis of reduction pretreatment process by multi-phase field method
Materials Research Express, 2020 The reduction pretreatment (RP) process is an effective method to improve billet quality, and the deformation recrystallization plays an important role in the process.
Hongqiang Liu +5 more
doaj +1 more source
Journal of Materials Research and Technology, 2023 The hot-working behavior of high-Mn austenitic steel for liquefied natural gas carriers at the deformation temperature in the range of 1073–1273 K and the strain rate in the range of 0.01–10 s−1 was studied on a Gleeble-3800 thermomechanical simulator ...
Peng Zhang +9 more
doaj +1 more source
Microstructure control during twin roll casting of an AZ31 magnesium alloy [PDF]
, 2012 The existing twin roll casting technique for magnesium alloys suffers heterogeneity in both microstructure and chemistry and downstream processing is required to improve the strip quality, resulting in cost rise.
Ferry M, I Bayandorian, Y Huang, Z Fan
core +1 more source
Journal of Materials Research and Technology, 2021 The hot deformation behavior of low-density high-strength Fe–Mn–Al–C steel at T = 900–1150 °C and ε˙ = 0.01–10 s−1 is studied using the Gleeble-3500 thermo-mechanical simulator.
Peng Wan +5 more
doaj +1 more source
Zjemňování zrna protlačované hořčíkové slitiny AZ31 procesem Ecap [PDF]
, 2017 Extruded Mg – 3%Al – 1% Zn (AZ31) magnesium alloy was subjected to ECAP (Equal Channel Angular Pressing) processing at 523 K (250 °C). At the processing temperature of 523 K, fine grains with the average grain size of 2 – 3 μm are formed as a result of ...
Hilšer, Ondřej +3 more
core +1 more source
Dynamic Recrystallization of Torsion Deformed NiAl
Materials Science Forum, 2005 Polycrystalline samples of NiAl have been deformed in torsion in the temperature range 800K – 1300K. Deformation is accompanied by dynamic recrystallization, which with increasing temperature changes from continuous to discontinuous mode. Emphasis was put on the occurrence of continuous dynamic recrystallization, which will be discussed with respect to
Klöden, B. +3 more