Forecast of the fatigue crack initiation site of commercially pure Titanium miniature specimens with local surface topography data [PDF]
MATEC Web of Conferences, 2020 Surfaces of technical components rarely appear in perfectly smooth condition. During fatigue loading, stress concentrations at surface asperities cause localized plastic deformation that can lead to crack initiation.
Böhme L. +4 more
doaj +1 more source
Materials & Design, 2020 Working service of structural materials at elevated temperatures generally leads to a significant decrease in their fatigue performance, thereby threatening the safety and reliability of engineering structures.
Xue Li +8 more
doaj +1 more source
Near-threshold fatigue crack growth in bulk metallic glass composites [PDF]
, 2009 A major drawback in using bulk metallic glasses (BMGs) as structural materials is their extremely poor fatigue performance. One way to alleviate this problem is through the composite route, in which second phases are introduced into the glass to arrest ...
Boopathy, Kombaiah +3 more
core +1 more source
Fracture and Structural Integrity, 2020 To meet the design requirements, different types of defects are often machined on the surface of fatigue components. Local stress concentration formed at the notch accelerates the initiation of fatigue crack, therefore greatly shortens the service lives ...
Zhi-qiang Wang +2 more
doaj +1 more source
Early slip activity and fatigue crack initiation of a near alpha titanium alloy [PDF]
MATEC Web of Conferences, 2020 For titanium alloys, crack initiation as a result of plastic strain accumulation has been shown to govern fatigue life under the high cycle fatigue regime.
Liu Conghui +3 more
doaj +1 more source
A fatigue crack initiation model incorporating discrete dislocation plasticity and surface roughness [PDF]
, 2007 Although a thorough understanding of fatigue crack initiation is lacking, experiments have shown that the evolution of distinct dislocation distributions and surface roughness are key ingredients.
Brinckmann, Steffen +1 more
core +4 more sources
MATEC Web of Conferences, 2018 Cyclic torsional fatigue properties of a high strength steel 100Cr6 are investigated using an ultrasonic torsional fatigue testing machine, and the results are compared with those obtained with fatigue tests under axial loading.
Xue Hongqian +3 more
doaj +1 more source
Advances on creep–fatigue damage assessment in notched components [PDF]
, 2017 In this paper, the extended Direct Steady Cyclic Analysis method (eDSCA) within the Linear Matching Method Framework (LMMF) is combined with the Stress Modified Ductility Exhaustion method and the modified Cavity Growth Factor (CGF) for the first time ...
Barbera, D., Chen, H., Liu, Y.
core +2 more sources
Jixie qiangdu, 2020 The fatigue crack initiation of the fuselage structure skin under the uniform supercharged cyclic load of 0 ～ 7. 8 Psi was experimentally studied by the self-made aircraft fuselage skin uniform supercharged fatigue simulation device.
LIU LiPing +5 more
doaj
Advances in Mechanical Engineering, 2022 To investigate the causes of damage dispersion in fatigue life of alloy materials, fatigue tests on 42CrMo are carried out under microscope with the aid of a micro fatigue testing device.
Nan Xu +4 more
doaj +1 more source