Thermomechanical Fatigue and Creep–Fatigue Interaction of Inconel 718 Additively Manufactured by Laser Beam Powder Bed Fusion

Advanced Engineering Materials, EarlyView.
Thermomechanical fatigue tests of laser beam powder bed fusion (PBF‐LB) Inconel 718 show that the additively manufactured material reaches almost the lifetimes of conventionally‐rolled material under no‐dwell conditions. Introducing dwell times at the maximum temperature markedly reduces the lifetimes due to pronounced grain boundary sliding associated
Stefan Guth, Tomáš Babinský, Jan Lars Riedel, Wen Hao Kan, Aijun Huang, Martin Heilmaier, Ivo Šulák   +6 more
wiley   +1 more source

In-situ SEM-EBSD investigation of the low-cycle fatigue deformation behavior of Inconel 718 at grain-scale

Journal of Materials Research and Technology, 2023
The low-cycle fatigue (LCF) deformation behavior of the Inconel 718 (IN718) specimen with micro-notch was investigated by an in-situ fatigue test inside a scanning electron microscope (SEM) combined with electron backscattered diffraction (EBSD).
Guanghao Guo, Wenxiang Jiang, Xuan Liu, Jutian Chen, Longyu Li, Jin Wang, Yuefei Zhang, Ze Zhang   +7 more
doaj   +1 more source

Karl Popper and the Mechanisms of Hydrogen Embrittlement

Advanced Engineering Materials, EarlyView.
Representation of the beginning of loss of ductility rather than embrittlement. Small concentrations of hydrogen in a diffusible form within iron are well‐established to harm the mechanical integrity of steels. There are theories that attempt to explain the pernicious role of hydrogen.
H. K. D. H. Bhadeshia
wiley   +1 more source

Microstructure‐Controlled Crack Propagation and Fracture Resistance in MoSiBTiC Alloy Revealed by Multiscale Extended Finite Element Method Modeling

Advanced Engineering Materials, EarlyView.
A two‐dimensional multiscale finite element analysis framework was established for the first‐generation MoSiBTiC alloy, and the mechanical and fracture‐related parameters of the constituent phases were calibrated through experiments and simulations. The framework provides a basis for analyzing crack propagation behavior in its complex microstructure ...
Junfeng Du, Takahiro Kaneko, Xinyu Yan, Takahito Ohmura, Kyosuke Yoshimi   +4 more
wiley   +1 more source

Hydrogen‐Assisted Fracture of Iron‐Based Fe–Ni–Al Alloys

Advanced Engineering Materials, EarlyView.
Principal relations and fracture mechanisms of single‐phase and precipitate‐strengthened Fe–Ni–Al alloys subjected to prior electrochemical hydrogen charging are identified. The mechanisms of hydrogen effect on strength and microhardness are discussed, including hydrogen‐induced increase in microhardness and the role of hydrogen in fracture behavior ...
Nataliya Yadzhak, Olha Zvirko, Rostyslav Leshchak, Hryhoriy Nykyforchyn   +3 more
wiley   +1 more source

High-cycle Rotate Bending Fatigue Behavior of TC17 at Elevated Temperature

工程科学与技术, 2014
:Rotating bending (50 Hz)fatigue tests were performed at room temperature,200 ℃ and 350 ℃,respectively,to evaluate the influence of temperature on the fatigue resistance and fatigue crack growth rates of TC17 alloy.Variation of sample deflection was used
李久楷, 刘永杰, 王清远, 侯方
doaj  

Slip Localization Intensification Mediated by Grain Boundary Sliding in a Polycrystalline Nickel‐Based Superalloy

Advanced Engineering Materials, EarlyView.
The temperature dependence of fatigue behavior in nickel‐based superalloys is investigated through high‐resolution measurements of plastic localization. While increasing temperature reduces localization and enhances fatigue performance in René 88DT, Inconel 718 exhibits a sharp degradation at intermediate temperature due to intensified slip ...
M. Calvat, D. Anjaria, I. Woo, C. Bean, D. Texier, J. C. Stinville   +5 more
wiley   +1 more source

Fatigue Crack Initiation and Growth in Nanocrystalline Ni at Multiple Length‐Scales

Advanced Engineering Materials, EarlyView.
Overview of miniaturized in situ SEM fatigue setup and resultant fatigue crack growth data for nanocrystalline Ni. The presented study focuses on the analysis of fatigue crack growth rate (FCGR) in focused ion beam‐notched microcantilevers prepared from nanocrystalline (NC) Ni as a model material.
Igor Moravcik, Alexander Jelinek, Markus Alfreider, Jutta Luksch, Anton Hohenwarter, Florian Schaefer, Christian Motz, Daniel Kiener   +7 more
wiley   +1 more source

Crack path in aeronautical titanium alloy under ultrasonic torsion loading

Fracture and Structural Integrity, 2015
This paper discusses features of fatigue crack initiation and growth in aeronautical VT3-1 titanium alloy under pure torsion loading in gigacycle regime. Two materials: extruded and forged VT3-1 titanium alloys were studied.
A. Nikitin, C. Bathias, T. Palin-Luc, A. Shanyavskiy   +3 more
doaj  

Effect of heat treatment on fatigue crack initiation of laser powder bed fusion stainless steel 316L

MATEC Web of Conferences, 2018
Laser powder bed fusion (L-PBF) is an emerging additive manufacturing technique for building structural components. L-PBF processing defects, such as lack of fusion pores, promote fatigue crack initiation and shorten the fatigue life.
Zhang Meng, Sun Chen-Nan, Zhang Xiang, Goh Phoi Chin, Wei Jun, Hardacre David, Li Hua   +6 more
doaj   +1 more source