Hydrogen‐Assisted Fracture of Iron‐Based Fe–Ni–Al Alloys
Advanced Engineering Materials, EarlyView.Principal relations and fracture mechanisms of single‐phase and precipitate‐strengthened Fe–Ni–Al alloys subjected to prior electrochemical hydrogen charging are identified. The mechanisms of hydrogen effect on strength and microhardness are discussed, including hydrogen‐induced increase in microhardness and the role of hydrogen in fracture behavior ...
Nataliya Yadzhak +3 more
wiley +1 more source
Effect of grain boundary microstructure on fatigue crack propagation in ferritic stainless steel
Nihon Kikai Gakkai ronbunshu, 2018 Effect of grain boundary microstructure, such as the spatial distribution and the connectivity of grain boundaries with different character, on the process of fatigue crack propagation in SUS430 ferritic stainless steel was investigated using the ...
Weitao YANG +2 more
doaj +1 more source
Predicting fatigue crack growth rate in a welded butt joint: The role of effective R ratio in accounting for residual stress effect [PDF]
, 2009 A simple and efficient method is presented in this paper for predicting fatigue crack growth rate in welded butt joints. Three well-known empirical crack growth laws are employed using the material constants that were obtained from the base material ...
Servetti, Guido, Zhang, X.
core +1 more source
Advanced Engineering Materials, EarlyView.The temperature dependence of fatigue behavior in nickel‐based superalloys is investigated through high‐resolution measurements of plastic localization. While increasing temperature reduces localization and enhances fatigue performance in René 88DT, Inconel 718 exhibits a sharp degradation at intermediate temperature due to intensified slip ...
M. Calvat +5 more
wiley +1 more source
Fatigue Crack Initiation and Growth in Nanocrystalline Ni at Multiple Length‐Scales
Advanced Engineering Materials, EarlyView.Overview of miniaturized in situ SEM fatigue setup and resultant fatigue crack growth data for nanocrystalline Ni. The presented study focuses on the analysis of fatigue crack growth rate (FCGR) in focused ion beam‐notched microcantilevers prepared from nanocrystalline (NC) Ni as a model material.
Igor Moravcik +7 more
wiley +1 more source
Fatigue damage evaluation of 316LN stainless steel using acoustic emission monitoring
工程科学学报, 2018 The initiation and growth of fatigue cracks usually lead to serious fatigue failure of steel structures such as pressure vessels and pipelines. Therefore, for the safety and reliability of engineering structures, monitoring the fatigue crack growth and ...
ZHANG Jin +3 more
doaj +1 more source
Phenomenological investigation of the influence of Cathodic protection on corrosion fatigue crack propagation behaviour, in a BS 4360 50D type structural steel and associated weldment microstructures, in a marine environment. [PDF]
, 1984 The influence of Cathodic Protection potential upon corrosion fatigue crack propagation rates in a medium7strength ferritic-pearlitic structural steel (ES 4360 grade 50D) and associated weldment microstructures in simulated sea-water was studied and ...
Thompson, J. W. C.
core
Surface Crack Shape Evolution Modelling using an RMS SIF approach [PDF]
, 2010 The majority of fatigue cracks in thick plate and tubular sections in structural components are two-dimensional surface cracks having significant propagation lives before becoming critical.
Han, S. K. +2 more
core +1 more source
Influence of Test Temperature and Test Frequency on Fatigue Life of Aluminum Alloy EN AW‐2618A
Advanced Engineering Materials, EarlyView.The influence of test temperature and test frequency on the fatigue life of EN AW‐2618A is investigated. High‐cycle fatigue tests are performed at different test temperatures and frequencies on the 1000 h/230°C overaged state. Both test parameters reduce fatigue life due to time‐dependent damage mechanisms.
Ying Han +5 more
wiley +1 more source
A crack-like notch analogue for a safe-life fretting fatigue design methodology
, 2003 Various analogies have recently been proposed for comparing the stress fields induced in fretting fatigue contact situations, with those of a crack and a sharp or a rounded notch, resulting in a degree of uncertainty over which model is most appropriate ...
Ciavarella, M., M. CIAVARELLA
core +1 more source