Advances in Materials Science and Engineering, 2020 In this paper, the effect of the fiber/matrix interface properties on the tensile and fatigue behavior of 2D woven SiC/SiC ceramic-matrix composites (CMCs) is investigated.
Longbiao Li
doaj +1 more source
Improvement of stress corrosion cracking resistance by low cycle fatigue of a CrNiMoV steel
npj Materials Degradation, 2023 Low cycle fatigue often interacts with stress corrosion cracking behavior. In this work, the effect of low cycle fatigue on stress corrosion cracking susceptibility of a CrNiMoV steel was investigated by interrupted fatigue tests in air and slow strain ...
Yu-Hui Huang +4 more
doaj +1 more source
Transportation Engineering, 2021 Asphalt components have a significant contribution to the fatigue cracking resistance of asphalt mixes. Softer asphalt binders, characterized through the Superpave grading system, resist fatigue cracking more than stiffer binders.
Eslam Deef-Allah, Magdy Abdelrahman
doaj +1 more source
Fatigue crack surface area and crack front length: new ways to look at fatigue crack growth [PDF]
MATEC Web of Conferences, 2018 This paper discusses the appropriateness of crack length as a reference dimension for fatigue damage. Current discussion on short crack versus long crack data is still divided between various approaches to model small crack growth. A proper physical explanation of the probable cause of the apparent differences between short crack and long crack data is
van Kuijk, J.J.A. (author) +2 more
openaire +4 more sources
Fatigue crack growth in a laser shock peened residual stress field [PDF]
, 2019 Laser Shock Peening is a surface treatment technique used in the aerospace sector to increase fatigue life, as well as resistance to fretting fatigue and stress corrosion cracking.
Achintha +19 more
core +1 more source
Aerospace, 2023 As the core component of the flexible nozzle on solid rocket motors, the flexible joint relies on the shear deformation of its silicone rubber elastomers to achieve a large vector angle, and the joint is prone to fatigue failure when working under high ...
Jinyao Zhang +5 more
doaj +1 more source
Analysis on Fatigue Crack Initiation and Fatigue Crack Propagation in a Gear
SMART MOVES JOURNAL IJOSCIENCE, 2017 An effective gear design balances strength, durability, reliability, size, weight and cost. Because of the advantage of gear, gearbox was used widely. But its fault also brought many losses of the production and society. It was necessary to research and analysis on the dynamical behavior of the gear system.
Anand Mohan Singh, Mrs. Madhulata Sharma
openaire +1 more source
Mechanical Engineering Journal, 2017 The fatigue life of austenitic stainless steel is significantly reduced in the environment of a pressurized water reactor (PWR). One of the methods for evaluating the environmental effect involves the use of the environmental correction factor (Fen ...
Choongmoo SHIM +2 more
doaj +1 more source
Development of a fretting-fatigue mapping concept: The effect of material properties and surface treatments [PDF]
, 2009 Fretting-fatigue induced by combined localized cyclic contact motion and external bulk fatigue loadings may result in premature and dramatic failure of the contacting components.
Araújo +32 more
core +1 more source
Thermal fatigue cracking of die-casting dies [PDF]
Metalurgija, 2010 Die-casting dies are exposed to high thermal and mechanical loads. Thermal fatigue cracking of dies due to thermal cycling may importantly shorten the life-time of the die.
Thermal fatigue cracking of die-casting dies +4 more
doaj