Results 1 to 10 of about 49,810 (187)
Hot Deformation Behavior and Processing Map of GH901 Superalloy [PDF]
Metals, 2021 During the forging process GH901 superalloys easily produce cracks and defects, such as coarse crystals in tissues, which affect the performance of the alloy.
Rui Ma +4 more
doaj +4 more sources
Hot Deformation Behavior and Hot Processing Map of 50CrVA Spring Steel [PDF]
MetalsIt is important to explore the hot deformation behavior and establish the hot processing map of steel to design and optimize the hot rolling process. In this paper, 50CrVA spring steel was used as the experimental material.
Yang Zhao +3 more
doaj +3 more sources
Journal of Materials Research and Technology, 2023 In order to predict the hot workability of the material more accurately, this paper takes the hot deformation of IN617B as the example. The activation energy (Q) map, Zener-Hollomon parameter (Z) map, and hot processing map were established based on the ...
Rui Luo +8 more
doaj +2 more sources
Hot deformation behavior and hot processing map of 40%SiCp/Al composites
Fenmo yejin jishu, 2023 The hot workability of the 40%SiCp/Al composites (volume fraction) was studied by isothermal compression deformation on Glebble-1500D thermal simulated test machine at the deformation temperature of 350~500 ℃ under the strain rate of 0.01~10.00 s−1.
HAO Shiming +5 more
doaj +2 more sources
Hot deformation behavior and hot processing map of GH2132 alloy [PDF]
High Temperature Materials and ProcessesHot compression experiments were conducted on GH2132 alloy rods using a Gleeble-3500 thermal simulator to investigate the high-temperature rheological behavior of the alloy at temperatures of 950, 1,000, 1,050, and 1,100 °C and strain rates of 0.001, 0 ...
Yuan YuKang +6 more
doaj +2 more sources
Investigation on Hot Deformation Behavior and Hot Processing Map of BSTMUF601 Super-Alloy [PDF]
Metals, 2016 Isothermal compression tests of BSTMUF601 super-alloy in the temperature range of 950 °C–1200 °C and at the strain rates of 0.2 s−1, 5 s−1, 10 s−1 were performed on a Gleeble-1500D thermo-mechanical simulator.
Chaoyang Sun +3 more
doaj +2 more sources
Hot Deformation Behavior and Processing Map of High-Strength Nickel Brass [PDF]
Metals, 2020 The flow behavior of a new kind of high-strength nickel brass used as automobile synchronizer rings was investigated by hot compression tests with a Gleeble-3500 isothermal simulator at strain rates ranging from 0.01 to 10 s−1 and a wide deformation ...
Qiang Liang +3 more
doaj +2 more sources
Hot deformation and processing map of Cr-Mo-B mechanical engineering steel
Cailiao gongcheng, 2019 The hot deformation behavior of Cr-Mo-B mechanical engineering steel was conducted at deformation temperature of 850-1150℃ and strain rates of 0.1-10s-1. The artificial neural network(ANN) model was developed based on the true stress-strain curves, where
SUN Ting +4 more
doaj +2 more sources
Dynamic recrystallization behavior and processing maps of 5CrNiMoV steel during hot deformation [PDF]
Materials Research Express, 2023 Hot deformation tests of 5CrNiMoV steel were performed at deformation temperatures of 700 to 870 °C and strain rates of 0.001 to 0.1 s ^−1 using the DIL 805D thermomechanical simulator.
Qin Li +3 more
doaj +2 more sources
Flow behavior and processing map of newly developed ECO-AlMag8 alloy during hot compression
Results in EngineeringThe flow behavior and processing map of ECO-AlMg8 alloy are investigated by hot compression of cylindrical samples machined from homogenized direct-chill cast billets at temperatures ranging from 300–450 °C and strain rates of 0.001 to 1 s⁻¹ using a ...
Majid Seyed Salehi +5 more
doaj +2 more sources