Potential fatigue strength improvement of AA 5083-H111 notched parts by wire brush hammering: Experimental analysis and numerical simulation [PDF]
, 2014 The effects of milling as machining process and a post-machining treatment by wire-brush hammering, on the near surface layer characteristics of AA 5083-H111 were investigated.
SIDHOM, Habib +4 more
core +1 more source
Temperature dependence of the interfacial shear strength in glass-fibre epoxy composites [PDF]
, 2014 The present work focuses on further investigation of the hypothesis that a significant fraction of apparent interfacial shear strength (IFSS) in fibre-reinforced composites can be attributed to a combination of residual radial compressive stress and ...
Thomason, James, Yang, Liu
core +1 more source
Study on the Variation of Mechanical Properties of Residual Plastic Film Over Time [PDF]
E3S Web of ConferencesThe mechanical properties of residual plastic film determine the recovery rate of residual film. The mechanical properties of residual film with a thickness of 0.01mm commonly used in the semi-arid region of northeastern China were tested at different ...
Zhang Dingguo, Song Zhe, Zhang Yaxin
doaj +1 more source
Interface strength in glass fibre-polypropylene measured using the fibre pull-out and microdebond methods [PDF]
, 2009 Interface strength in glass fibre-polypropylene was measured using both fibre pull-out and microdebond methods. Excellent compatibility between two methods was obtained. The data from microdebond test could be divided into two groups according to whether
Thomason, James +3 more
core +5 more sources
Methods of measuring residual stresses in components [PDF]
, 2012 Residual stresses occur in many manufactured structures and components. Large number of investigations have been carried out to study this phenomenon and its effect on the mechanical characteristics of these components.
Olabi, Abdul-Ghani +10 more
core +2 more sources
Fibers, 2021 The bending performance of a basalt-polypropylene fiber-reinforced concrete (HBPFRC) was characterized by testing 24,400 × 100 × 100 mm3 prismatic specimens in a four-point bending test JSCE-SF4 configuration.
Zhiyun Deng +4 more
doaj +1 more source
IMPACT BEHAVIOUR AND RESIDUAL STRENGTH OF HONEYCOMB STRUCTURES [PDF]
Annals: Series on engineering sciences (Academy of Romanian Scientists), 2014 The goal of this article is to study the behavior of sandwich structures with honeycomb core during and after an impact. In this purpose, a test program was created and afterwards was applied.
Horia Alexandru PETRESCU, Anton HADAR
doaj
Archives of Foundry Engineering, 2017 This study shows the results of the investigation of the strength performance, and residual strength of a single component inorganic binder system Cast Clean S27®. The study was conducted using three different foundry sand sources in South Africa. Sample
Banganayi F.C, Nyembwe K, Polzin H
doaj +1 more source
Evaluation of the survivability of CFRP honeycomb-cored panels in compression after impact tests
Fracture and Structural Integrity, 2021 This paper is oriented to the experimental research of the mechanics of the CFRP sandwich plates, glass and carbon fiber sample panels with a large-cell honeycomb core.
Oleg A. Staroverov +2 more
doaj +1 more source
Synchrotron strain scanning for residual stress measurement in cold-drawn steel rods [PDF]
, 2011 Cold-drawn steel rods and wires retain significant residual stresses as a consequence of the manufacturing process. These residual stresses are known to be detrimental for the mechanical properties of the wires and their durability in aggressive ...
M Elices +5 more
core +1 more source